Low-denier nylon fabric compounding process

A technology of nylon fabric and composite process, which is applied in the direction of layered products, lamination devices, lamination, etc., can solve the problems of affecting the softness of the fabric, overflowing glue, affecting the color fastness, etc., to avoid repeated glue coating, fiber structure, etc. Fluffy, efficiency-enhancing effect

Pending Publication Date: 2021-02-05
上海韬睿纺织科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Due to the tight fiber structure of traditional low-denier nylon fabrics before compounding, the dyes cannot penetrate faster and better, which not only increases the dyeing time, but also affects the dyeing fastness. In addition, the existing fabrics pass through during compounding. The gluing roller rol

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-denier nylon fabric compounding process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The present invention proposes a low-denier nylon fabric compounding process, which includes the following steps: base fabric finishing, film covering, pressing, standing maintenance, specifically including the following steps:

[0024] Step S1, select the base fabric that meets the quality inspection standards, and obtain a base fabric suitable for coating after steps such as washing and drying, defibering, dyeing and drying, and padding and drying with finishing solution;

[0025] Step S2, covering the front and back of the base fabric with a low-denier nylon film by a laminating device, and sticking it with an adhesive to obtain a low-denier nylon composite fabric;

[0026] Step S3, pressing the composite fabric, so that the nylon film and the base fabric are completely bonded, and the overflow glue is removed;

[0027] Step S4, standing the composite fabric at a temperature range of 140-180°C, so that the adhesive is naturally and fully integrated between the base f...

Embodiment 2

[0035] The present invention proposes a low-denier nylon fabric compounding process, which includes the following steps: base fabric finishing, film covering, pressing, standing maintenance, specifically including the following steps:

[0036] Step S1, select the base fabric that meets the quality inspection standards, and obtain a base fabric suitable for coating after steps such as washing and drying, defibering, dyeing and drying, and padding and drying with finishing solution;

[0037] Step S2, covering the front and back of the base fabric with a low-denier nylon film by a laminating device, and sticking it with an adhesive to obtain a low-denier nylon composite fabric;

[0038] Step S3, pressing the composite fabric, so that the nylon film and the base fabric are completely bonded, and the overflow glue is removed;

[0039] Step S4, standing the composite fabric at a temperature range of 140° C., so that the adhesive is naturally and fully integrated between the base fab...

Embodiment 3

[0047] The present invention proposes a low-denier nylon fabric compounding process, which includes the following steps: base fabric finishing, film covering, pressing, standing maintenance, specifically including the following steps:

[0048] Step S1, select the base fabric that meets the quality inspection standards, and obtain a base fabric suitable for coating after steps such as washing and drying, defibering, dyeing and drying, and padding and drying with finishing solution;

[0049] Step S2, covering the front and back of the base fabric with a low-denier nylon film by a laminating device, and sticking it with an adhesive to obtain a low-denier nylon composite fabric;

[0050] Step S3, pressing the composite fabric, so that the nylon film and the base fabric are completely bonded, and the overflow glue is removed;

[0051] Step S4, standing the composite fabric at a temperature range of 180°C, so that the adhesive is naturally and fully integrated between the base fabri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a low-denier nylon fabric compounding process, which comprises the following steps of base cloth finishing, film coating, pressing and standing maintenance, and specifically comprises the following steps of S1, selecting base cloth meeting the quality inspection standard, and performing the steps of cleaning and drying, fiber yarn removing, dyeing and drying, finishing liquid padding and drying and the like to obtain base cloth fabric suitable for film coating, and S2, coating the front side and the back side of the base fabric with low-denier nylon films through coating equipment, and adhering through an adhesive to obtain a low-denier nylon composite fabric. Before the composite fabric is dyed, the refining agent and the oil removing agent are used for scouring the base fabric, so that the dyeing efficiency and the dyeing fastness are improved; by means of the design that the glue plug is elastically connected into the glue penetrating hole of the gluing roller, glue can only be discharged from the contact position of the gluing roller and the fabric, glue cannot be discharged from other non-contact positions, the surface of the fabric can be evenly smeared when the glue is smeared, and repeated gluing is avoided.

Description

technical field [0001] The invention relates to a fabric compounding process, in particular to a low-denier nylon fabric compounding process. Background technique [0002] The compounding of fabrics is a new type of material formed by bonding one or more layers of textile materials, non-woven materials and other functional materials, such as low-denier nylon film obtained by compounding low-denier nylon film and base fabric. Fabric composite. It is suitable for making sofas, clothing and other textiles. It is one of the indispensable fabrics for people's home life. It is made of superfine fibers in specific textile processing and unique dyeing and finishing, and then processed by "composite" equipment. Since the composite fabric adopts superfine fibers, the fabric has high cleaning ability, that is, decontamination ability. [0003] Due to the tight fiber structure of traditional low-denier nylon fabrics before compounding, the dyes cannot penetrate faster and better, whic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B37/10B32B37/12B32B37/06
CPCB32B37/10B32B37/1284B32B37/06
Inventor 石峰
Owner 上海韬睿纺织科技有限公司