Bridge deck waterproof material and preparation method thereof

A waterproof material and powder technology, applied in the field of waterproof materials, can solve the problems of poor temperature stability of the asphalt layer, shortened service life of the road surface, difficult to guarantee durability, etc., and achieves good waterproofness, improved high temperature resistance and stable performance. Effect

Active Publication Date: 2021-03-02
深圳市欧名朗实业发展有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the temperature stability of the unmodified asphalt layer is poor, it is easy to be brittle in winter, and it is easy to soften in summer; it has poor aging resistance and durability is not easy to guarantee; the mainte

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] The preparation method of the N-(3-acryloyloxy-2-hydroxypropyl)-3-aminopropyltriethoxysilane modified vegetable oil comprises: N-(3-acryloyloxy-2 -Hydroxypropyl)-3-aminopropyltriethoxysilane, vegetable oil, and catalyst were added into the reaction kettle, and stirred and reacted at normal pressure and 30-50°C for 10-15 hours.

[0027]The mass ratio of the N-(3-acryloxy-2-hydroxypropyl)-3-aminopropyltriethoxysilane, vegetable oil and catalyst is 0.1:(2-4):(0.05-0.15) .

[0028] The vegetable oil is at least one of rapeseed oil, castor oil, palm oil, peanut oil and olive oil.

[0029] The catalyst is formed by mixing tetrabutyl titanate, tetrabutylammonium bromide, and graphene quantum dots in a mass ratio of 1:2:(0.03-0.05).

[0030] The initiator is at least one of azobisisobutyronitrile and azobisisoheptanonitrile; the emulsifier is sodium dodecylbenzenesulfonate, polyoxypropylene polyoxyethylene glyceryl ether, nonylphenol One or more of polyoxyethylene ethers.

...

Embodiment 1

[0041] Embodiment 1 provides a bridge deck waterproof material, which is characterized in that it is composed of a liquid component and a powder, and the liquid component includes the following components by weight: 10 parts of acrylic polyurethane emulsion, asphalt modified 8 parts of waterproof emulsion, 3 parts of carboxyl-terminated liquid fluororubber, 2 parts of N-(3-acryloyloxy-2-hydroxypropyl)-3-aminopropyltriethoxysilane modified vegetable oil, 0.1 part of initiator , 70 parts of water, 0.5 part of emulsifier; the powder is made of the following components in parts by weight: 80 parts of cement, 15 parts of silica sand, 3 parts of corundum, 1 part of nano boron fiber, functional modified aluminum 1 part of metal organic framework; the mass ratio of the liquid component to the powder is 1:3.

[0042] The preparation method of the N-(3-acryloyloxy-2-hydroxypropyl)-3-aminopropyltriethoxysilane modified vegetable oil comprises: N-(3-acryloyloxy-2 -Hydroxypropyl)-3-aminop...

Embodiment 2

[0048] Embodiment 2 provides a bridge deck waterproof material, its formulation and preparation method are basically the same as in Embodiment 1, the difference is that it is composed of a liquid component and a powder, and the liquid component includes the following by weight: Various ingredients: 11 parts of acrylic polyurethane emulsion, 9 parts of asphalt modified waterproof emulsion, 3.5 parts of carboxyl-terminated liquid fluororubber, N-(3-acryloyloxy-2-hydroxypropyl)-3-aminopropyl triethyl 2.5 parts of oxysilane modified vegetable oil, 0.15 parts of initiator, 72 parts of water, and 0.7 part of emulsifier; the powder is made from the following components in parts by weight: 83 parts of cement, 17 parts of silica sand, 3.5 parts of corundum, 1.5 parts of nano-boron fiber, and 1.2 parts of functionally modified aluminum metal organic framework; the mass ratio of the liquid component to the powder is 1:3.5.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a bridge deck waterproof material, which is characterized by comprising a liquid component and powder, wherein the liquid component is prepared from the following components inparts by weight: 10-15 parts of an acrylic polyurethane emulsion, 8-12 parts of asphalt modified waterproof emulsion, 3-5 parts of carboxyl-terminated liquid fluororubber, 2-4 parts of N-(3-acryloyloxy-2-hydroxypropyl)-3-aminopropyl triethoxysilane modified vegetable oil, 0.1-0.3 part of an initiator, 70-80 parts of water and 0.5-1.5 parts of an emulsifier; wherein the powder is prepared from thefollowing components in parts by weight: 80-90 parts of cement, 15-25 parts of silica sand, 3-5 parts of carborundum, 1-3 parts of nano boron fibers and 1-2 parts of a functional modified aluminum metal organic framework; wherein the mass ratio of the liquid component to the powder is 1: (3-5). The invention further provides a preparation method of the bridge deck waterproof material. The bridgedeck waterproof material provided by the invention is good in waterproofness, excellent in aging resistance and durability, strong in bonding property with a bridge deck, excellent in high-temperatureresistance and performance stability and long in service life.

Description

technical field [0001] The invention relates to the technical field of waterproof materials, in particular to a bridge deck waterproof material and a preparation method thereof. Background technique [0002] With the rapid development of my country's highways, especially expressways, the number of highway bridges is increasing day by day, and all kinds of bridges are springing up like mushrooms, which bring a lot of convenience to people's transportation and create another beautiful road for modern cities. landscape. At the same time, the safety and service life of bridges have aroused widespread concern from domestic and foreign counterparts. [0003] At present, during the use of the bridge deck on the road, in rainy and snowy weather, the rainwater penetrates the asphalt concrete surface to reach the surface of the cement concrete. Due to the poor waterproof effect of the concrete, the water continues to infiltrate into the interior of the cement concrete of the bridge de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B111/27
CPCC04B28/04C04B2111/00293C04B2111/27C04B2201/10C04B2111/00508C04B2111/0075C04B14/06C04B14/324C04B14/38C04B24/40C04B24/282C04B24/36C04B24/2682C04B24/42C04B24/129C04B24/20
Inventor 程焕芹季路路
Owner 深圳市欧名朗实业发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap