Manufacturing method of q420gj medium-thick steel plate for low-yield ratio, low-cost and high-performance building structure

A technology of building structure and low yield ratio, applied in the field of metallurgy, can solve problems such as high yield ratio, achieve the effect of reducing production cost and simplifying production organization

Active Publication Date: 2021-12-10
LIUZHOU IRON & STEEL +1
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a method for manufacturing Q420GJ medium-thick steel plates for low-yield-ratio low-cost high-performance building structures to solve the problem of high yield ratio of Q420GJ medium-thick steel plates

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of q420gj medium-thick steel plate for low-yield ratio, low-cost and high-performance building structure
  • Manufacturing method of q420gj medium-thick steel plate for low-yield ratio, low-cost and high-performance building structure
  • Manufacturing method of q420gj medium-thick steel plate for low-yield ratio, low-cost and high-performance building structure

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0052] Examples 1-1 Examples 1-2 are used in the chemical composition of Example 1, Example 1-1, Examples 1-2 are examples of different processes of Scheme 1;

example 2

[0053] Examples 2-1 Examples 2-2 are used in the chemical composition of Example 2, Examples 2-1, Examples 2-2 are examples of different processes of Scheme 2;

example 3

[0054] Examples 3-1 Examples 3-2 are used in the chemical composition of Example 3, Example 3-1, Examples 3-2 are examples of different processes of Scheme 1;

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
yield ratioaaaaaaaaaa
Login to View More

Abstract

The invention provides a manufacturing method for low -flexed and low -cost high -performance building structures in Q420GJ.It is C: 0.14WT % ~ 0.17WT %, SI: 0.20WT % ~ 0.40WT %, Mn: 1.4WT % to 1.6WT %, P: ≤0.020WT %, S: ≤0.01wt %, Alt: 0.020 % ~0.050WT %, nb: 0.040WT % ~ 0.055WT %, V: 0.025WT % ~ 0.040WT %, TI: 0.015WT % ~ 0.030WT %, CEV: ≤0.44WT %, the balance is Fe and inevitable trace trace.Elements; Qu Qiang ratio 0.72‑0.78.The present invention can obtain Q420GJ with low flexion and high -cost qualified high -performance building structure.

Description

Technical field [0001] The present invention relates to the field of metallurgy, particularly to iron and steel manufacturing, in particular a low yield ratio high-performance low-cost method of manufacturing a building structure in a steel plate Q420GJ. Background technique [0002] Seismic steel building is the core issue of concern, and shock resistance and yield ratio of steel and is closely related. Yield ratio refers to the ratio of the yield strength and tensile strength of steel, which is an important index coefficient is a measure of the strength of the steel stock. Flexion strength steel material is relatively high, indicating a strong resistance to deformation of the materials, plastic deformation under external force hardly occurs, but the material is poor resistance to external shocks, the risk of brittle fracture is large, the reliability of the material low. Therefore, low yield ratio steel building structures is the seismic performance materials, safety and reliab...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C33/04C22C38/02C22C38/04C22C38/06C22C38/12C22C38/14C21C7/00C21C7/06C21C7/072
CPCC22C33/04C22C38/02C22C38/04C22C38/06C22C38/12C22C38/14C21C7/06C21C7/072C21C7/0006
Inventor 李显樊雷杨跃标肖娟李磊韦龙周朱鹏宇刘崇林李宗强陈盛淋廖耀俊
Owner LIUZHOU IRON & STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com