High-strength thin band steel for cold forming and manufacturing method thereof

A manufacturing method and technology of thin strip steel, applied in the field of continuous casting process, can solve the problems of uneven structure, poor formability, high yield ratio, achieve uniform grain structure, reduce the thickness of oxide scale, reduce rolling effect of temperature

Active Publication Date: 2012-11-28
BAOSHAN IRON & STEEL CO LTD
View PDF18 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0018] The purpose of the present invention is to provide a high-strength thin strip steel for cold forming and its manufacturing method, which can solve the problems of uneven structure, low elongation, high yield ratio and poor formability in the thin strip continuous casting process , to meet the use requirements of bending forming, stamping forming, etc., so as to meet the use requirements of cold-rolled base materials and "replacing cold with heat" products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength thin band steel for cold forming and manufacturing method thereof
  • High-strength thin band steel for cold forming and manufacturing method thereof
  • High-strength thin band steel for cold forming and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0105] see figure 1 , which shows the technological process of the present invention, molten steel is directly poured on a crystallization roller 5a, 5b and 5b which are relatively rotating and capable of rapid cooling through the ladle 1 through the ladle shroud 2, the tundish 3 and the flow distribution device 4 In the molten pool 7 surrounded by side sealing plate devices 6a, 6b, molten steel solidifies on the circumferential surface of the crystallization rollers 5a, 5b, and then forms a solidified shell, which gradually grows and then forms at the smallest gap between the two crystallization rollers (nip point). 1.5-3 mm thick cast strip 11 . The casting strip passes through the secondary cooling device 8 in the airtight chamber 10, and immediately sprays dry ice particles (solid CO 2 ), to control the cooling rate, so that the casting belt 11 is rapidly and uniformly cooled to below 1280°C. Then the cast strip is sent to the hot rolling mill 13 by swinging the guide p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to high-strength thin band steel for cold forming and a manufacturing method thereof. The method comprises the following steps: after discharging a cast band from a crystal roll, cooling the cast band forcibly and uniformly in a mode of spraying dry ice under high pressure; quickly cooling the cast band to be below 1,280 DEG C at the cooling speed of 200-300 DEG C / s; performing austenite on-line recrystallization rolling, wherein the rolling temperature is 1,050 to 1,200 DEG C and the rolling reduction is 20 to 50 percent; and quickly cooling the band steel subjected to hot rolling in an anti-oxidation mode, wherein the anti-oxidation quick cooling speed is 80 to 200 DEG C / s and the reeling temperature is 500 to 600 DEG C. By the method, the high-strength thin band steel for automobile cold forming and with low yield strength and excellent stamping performance can be obtained, can be directly used in a mode of substituting heat for cold, cancels the cold rolling procedure and greatly reduces the production cost.

Description

technical field [0001] The invention belongs to the continuous casting process, in particular to a high-strength thin steel strip for cold forming and a manufacturing method thereof. Background technique [0002] In the traditional steel production process, tin (Sn) is a typical residual element or harmful element in steel. It is very difficult and expensive to fully remove Sn in the steelmaking process. Once Sn is contained in steel, it is basically impossible to completely eliminate it. , can only reduce the content of Sn by diluting molten steel, all of which lead to the increase of the cost of steel products. [0003] In recent years, due to the continuous recycling of scrap steel, the content of residual elements such as Sn in steel has gradually increased. Sn in steel is an element that is easy to segregate, and it is easy to be enriched at the grain boundary to cause defects such as cracks. Therefore, in the traditional process The content of Sn element in steel is s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/14C22C38/12B22D11/06C21D8/02
Inventor 吴建春方园于艳
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com