Antibacterial and antiviral inorganic decorative plate and preparation method thereof

A decorative plate, anti-virus technology, applied in the directions of botanical equipment and methods, disinfectants, fungicides, etc., can solve the problem of lack of anti-bacterial and anti-viral decorative plates

Inactive Publication Date: 2021-04-23
湖北格林森绿色环保材料股份有限公司
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem solved by the present invention is: provide an antibacterial and antiviral inorganic decorative plate and its preparation method, to solve the technical problem in the prior art that there is no effective antibacterial and antiviral decorative plate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial and antiviral inorganic decorative plate and preparation method thereof
  • Antibacterial and antiviral inorganic decorative plate and preparation method thereof
  • Antibacterial and antiviral inorganic decorative plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] Such as figure 1 Shown, a kind of preparation method of the inorganic decorative sheet material with antibacterial and antiviral, specifically comprises the following steps (the allocation of following each raw material is all by weight):

[0052] S1. Preparation of antibacterial and antiviral active liquid: After 62 parts of pomegranate peel, 8 parts of mugwort, 10 parts of Houttuynia cordata, 10 parts of camphor leaves, and 10 parts of olive leaves, they are successively crushed into 180 meshes, and pressed with 70% ethanol for 1 : 12 solid-liquid ratio soaking for 4.5h, ultrasonic extraction for 30min, heating and evaporation after vacuum filtration, heating temperature 70°C, heating time 30min, evaporation to 100 parts, 6 parts for later use;

[0053] S2. Preparation of porous mineral carrier: 80 parts of diatomite, 10 parts of sepiolite, 10 parts of attapulgite, fineness requirement ≥ 180 mesh, stir evenly, take 12 parts for later use;

[0054] S3. Preparation of ...

Embodiment 2

[0063] A preparation method of an inorganic decorative plate with antibacterial and antiviral properties, specifically comprising the following steps (the allocation of the following raw materials is by weight):

[0064] S1. Preparation of antibacterial and antiviral active liquid: 90 parts of pomegranate peel, 10 parts of Houttuynia cordata, 2 parts of mugwort, 2 parts of Houttuynia cordata, 2 parts of camphor leaves, and 2 parts of olive leaves were sequentially crushed into 180 meshes, and Soak in 72% ethanol for 6 hours at a material-to-liquid ratio of 1:15, ultrasonically extract for 45 minutes, vacuum filter and then heat and evaporate at a heating temperature of 68°C for a heating time of 30 minutes, evaporate to 100 parts, and take 12 parts for later use;

[0065] S2. Preparation of porous mineral carrier: 3 parts of diatomaceous earth for backup.

[0066] S3. Preparation of inorganic gelled powder: 59 parts of desulfurized gypsum for standby.

[0067] S4. Preparation...

Embodiment 3

[0075] A preparation method of an inorganic decorative plate with antibacterial and antiviral properties, specifically comprising the following steps (the allocation of the following raw materials is by weight):

[0076] S1. Preparation of antibacterial and antiviral active liquid: 62 parts of pomegranate peel, 8 parts of mugwort, 10 parts of Houttuynia cordata, 10 parts of camphor leaves, and 10 parts of olive leaf are sequentially pulverized into 180 meshes, and press 1:1 with 68% ethanol 10 Material-to-liquid ratio Soak for 36 hours, ultrasonically extract for 50 minutes, heat and evaporate after vacuum filtration, heating temperature is 72°C, heating time is 30 minutes, evaporate to 100 parts, take 16.8 parts for later use;

[0077] S2. Preparation of porous mineral carrier: take 3 parts of diatomite and 1 part of attapulgite and mix well for later use.

[0078] S3. Preparation of inorganic gelling powder: mix 5 parts of high-strength gypsum powder, 88 parts of ordinary na...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an antibacterial and antiviral inorganic decorative plate and a preparation method thereof. The antibacterial and antiviral inorganic decorative plate comprises the following components by weight percentage: 42-66% of inorganic gelling powder, 25-31.6% of surface modification solution, 5.3-16.8% of plant antibacterial and antiviral active solution, 2.67-8.44% of porous mineral carrier, 0.05-8.4% of reinforcing fiber, and 2-10% of modifier in the surface modification solution. The weight percentage of the antibacterial and antiviral active substances in the plant antibacterial and antiviral active liquid is 38%-65%. The inorganic decorative plate with the antibacterial and antiviral functions has the advantages of wide antibacterial and antiviral range, better antibacterial and antiviral properties, low plate preparation cost and low use cost for killing bacteria and viruses by using the inorganic decorative plate with the antibacterial and antiviral functions.

Description

technical field [0001] The invention belongs to the technical field of decorative plates, and in particular relates to an antibacterial and antiviral inorganic decorative plate and a preparation method thereof. Background technique [0002] There are various volatile and harmful organic compounds, bacteria and viruses in people's living environment, which directly affect people's physical and mental health. The development of decorative panels that remove organic matter, anti-bacteria and viruses not only meets the decoration needs, but also ensures the safety of the living environment sex is of great significance. [0003] "A kind of algae-calcium composite material, decorative board and production method" (CN102515678A) discloses a decorative board, which is composed of a calcium-containing inorganic matrix and an algae-based hydration gel. The product has excellent formaldehyde purification, negative ion Inducible, self-humidity and other ecological properties; "A Photoc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/16C04B28/14C04B41/62A01N65/24A01N65/12A01N65/08A01P3/00A01P1/00C04B111/20
CPCC04B28/16C04B28/143C04B28/144C04B41/62C04B41/009C04B41/463A01N65/00A01N65/24A01N65/12A01N65/08C04B2111/2092
Inventor 韦华童潇雨冯林
Owner 湖北格林森绿色环保材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap