Anti-radiation ceramic tile adhesive mortar and preparation method thereof

A bonding mortar and anti-radiation technology, which is applied in the field of ceramic tile bonding mortar production, can solve problems such as not having radiation protection performance, and achieve the effects of excellent radiation protection performance, excellent adhesion, and aging resistance

Pending Publication Date: 2021-09-17
河北三棵树涂料有限公司
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the shortcomings of the existing ceramic tile adhesive mortar which has excellent adhesion, crack resistance, hollowing resistance, aging resistance, and low price, but does not have radiation protection performance, the present invention provides a radiation protection ceramic tile Adhesive mortar and its preparation method, using cement and redispersible latex powder as bonding material, using barium sulfate sand with optimal mesh and other graded sand except barium sulfate sand as filler, adding the function of radiation protection Material modified carbon powder, through the combination of barium sulfate sand and radiation-proof functional material modified carbon powder, with other preferred components and their dosage ratio, it has excellent radiation protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-radiation ceramic tile adhesive mortar and preparation method thereof
  • Anti-radiation ceramic tile adhesive mortar and preparation method thereof
  • Anti-radiation ceramic tile adhesive mortar and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of anti-radiation ceramic tile bonding mortar according to the present invention is mainly prepared from the following components according to the following ratios by weight and number:

[0028]

[0029] Wherein, the filler includes 15 parts of 40-70 mesh barium sulfate sand and 40 parts of 50-100 mesh quartz sand.

[0030] The preparation method of the radiation-proof ceramic tile bonding mortar mainly includes the following steps carried out in sequence:

[0031] (1) Put the cement into the stirring tank, turn on the stirring blade and the flying knife, the rotating speed of the main shaft stirring blade is 200r / min, and the rotating speed of the flying knife is 3000r / min, and then slowly add the high-grade material into the stirring tank while stirring. Then disperse the latex powder, cellulose ether, calcium formate and starch ether, and stir for 5 minutes;

[0032] (2) Keep the rotating speed of the main shaft stirring blade at 200r / min, and the rotating...

Embodiment 2

[0034] A kind of anti-radiation ceramic tile bonding mortar according to the present invention is mainly prepared from the following components according to the following ratios by weight and number:

[0035]

[0036]

[0037] Wherein, the filler includes 15 parts of 40-70 mesh barium sulfate sand and 10 parts of other graded sands except barium sulfate sand.

[0038] The preparation method of the radiation-proof ceramic tile bonding mortar mainly includes the following steps carried out in sequence:

[0039] (1) Put the cement into the stirring tank, turn on the stirring blade and the flying knife, the rotating speed of the main shaft stirring blade is 240r / min, and the rotating speed of the flying knife is 2500r / min, and then slowly add the high-grade material into the stirring tank while stirring. Then disperse the latex powder, cellulose ether, calcium formate and starch ether, and stir for 3 minutes;

[0040] (2) Keep the rotating speed of the main shaft stirring b...

Embodiment 3

[0042] A kind of anti-radiation ceramic tile bonding mortar according to the present invention is mainly prepared from the following components according to the following ratios by weight and number:

[0043]

[0044] Wherein, the filler includes 30 parts of 40-70 mesh barium sulfate sand and 40 parts of other graded sands except barium sulfate sand.

[0045] The preparation method of the radiation-proof ceramic tile bonding mortar mainly includes the following steps carried out in sequence:

[0046] (1) Put the cement into the stirring tank, turn on the stirring blade and the flying knife, the rotating speed of the main shaft stirring blade is 300r / min, and the rotating speed of the flying knife is 2000r / min, and then slowly add the high-grade material into the stirring tank while stirring. Then disperse latex powder, cellulose ether, calcium formate and starch ether, and stir for 6 minutes;

[0047] (2) Keep the rotating speed of the main shaft stirring blade at 300r / min...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to anti-radiation ceramic tile adhesive mortar and a preparation method thereof, and the anti-radiation ceramic tile adhesive mortar is mainly prepared from the following components in parts by weight: a filler comprises 15.0-30.0 parts of barium sulfate sand of 40-70 meshes and 10.0-40.0 parts of other fillers. The anti-radiation ceramic tile adhesive mortar overcomes the defects that ceramic tile adhesive mortar has excellent cohesiveness, cracking resistance, hollowing resistance and aging resistance, is low in price and does not have radiation resistance, cement and redispersible latex powder are used as adhesive materials, graded sand and barium sulfate sand with the preferable mesh number are used as fillers, functional material modified carbon powder with an anti-radiation function is added, and the barium sulfate sand and the anti-radiation functional material modified carbon powder are combined and matched with other preferable components and the dosage proportion thereof, so that the anti-radiation coating has excellent anti-radiation performance.

Description

technical field [0001] The invention relates to a radiation-proof tile bonding mortar and a preparation method thereof, which are applied in the field of tile bonding mortar production. Background technique [0002] As people's living standards are getting better and better, more and more electrical appliances are used in daily life, so the problems that affect human health caused by electromagnetic interference are becoming more and more serious. [0003] For people's health, it is very important to take measures to prevent electromagnetic interference. As an indispensable decoration material in interior decoration in recent years, tiles and tile bonding mortars are more and more widely used. Now commercially available tile bonding mortar has excellent adhesion, crack resistance, hollowing resistance, aging resistance, and low price, but it does not have radiation protection. If it has the function of radiation protection, it must be It will improve the electromagnetic en...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B14/06C04B14/36C04B14/38C04B14/02
CPCC04B28/00C04B14/368C04B14/06C04B14/386C04B14/024C04B2111/00637C04B2111/00258C04B2103/0057C04B24/383C04B14/106C04B24/04C04B24/38
Inventor 蒋克飞李小亮张少玉杨帅
Owner 河北三棵树涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap