Polymerizable eutectic solvent, conductive elastomer and preparation method thereof

A technology of deep eutectic solvent and elastomer, applied in the field of conductive elastomer and its preparation, polymerizable deep eutectic solvent, can solve the problems of poor mechanical properties, poor biocompatibility, liquid leakage, etc., and achieve high biocompatibility The effect of the property and the simple preparation method

Active Publication Date: 2022-02-15
JIANGNAN UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The existing polymerizable deep eutectic solvents have few types and poor biocompatibility. The existing elastomer preparation methods are complicated, have low biocompatibility, and may have problems such as liquid leakage and poor mechanical properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polymerizable eutectic solvent, conductive elastomer and preparation method thereof
  • Polymerizable eutectic solvent, conductive elastomer and preparation method thereof
  • Polymerizable eutectic solvent, conductive elastomer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A polymerizable deep eutectic solvent, the preparation process is as follows: 5.912g of hydrogen bond acceptor choline citrate and 5.647g of hydrogen bond donor 1-vinylimidazole were stirred and reacted at 60°C for 2h to obtain a clear polymerizable low eutectic solvent. eutectic solvent.

[0031] Properties: yellow flowable liquid at room temperature, see figure 1 .

Embodiment 2

[0033] A polymerizable deep eutectic solvent, the preparation process is as follows: 6.185g of hydrogen bond acceptor betaine citrate and 5.647g of hydrogen bond donor 2-vinylimidazole were stirred and reacted at 60°C for 2h to obtain a clear polymerizable low eutectic solvent. eutectic solvent.

[0034] Properties: It is a yellow flowable liquid at room temperature.

Embodiment 3

[0036] A kind of polymerizable deep eutectic solvent, its preparation process is as follows: 15.062g of hydrogen bond acceptor glutamate choline and 6.488g of hydrogen bond donor 2-methyl-1-vinylimidazole were stirred and reacted at 70°C for 1.5 h Obtained a clear polymerizable deep eutectic solvent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polymerizable eutectic solvent, a conductive elastomer and a preparation method thereof. The polymerizable eutectic solvent is obtained by blending a hydrogen bond acceptor and a hydrogen bond donor at 60-100 DEG C, the hydrogen bond acceptor comprises polycarboxylic acid choline and/or polycarboxylic acid betaine, the hydrogen bond donor comprises an imidazole monomer, and the molar ratio of the hydrogen bond donor to the hydrogen bond acceptor is not less than 1: 1. The elastomer comprises the polymerizable eutectic solvent, a cross-linking agent and an initiator, and is prepared under light or heat curing. The conductive elastomer prepared from the polymerizable eutectic solvent has unique ionic conductivity, good optical transparency and biocompatibility, and has wide application prospects in biosensors, wound healing, cell tissue engineering and motion monitoring.

Description

technical field [0001] The invention relates to a polymerizable low eutectic solvent, a conductive elastomer and a preparation method thereof, belonging to the technical field of ionic liquids. Background technique [0002] Deep eutectic solvents belong to the subclass of ionic liquids, which inherit the chemical stability and high conductivity of ionic liquids, and also have the advantages of low cost, 100% atom utilization, and simple preparation, which ionic liquids do not have. At present, the research on deep eutectic solvents mainly focuses on the fields of gas capture, biomass extraction and dissolution, and catalysis. The polymerizable deep eutectic solvent refers to a deep eutectic solvent capable of forming a conductive elastomer through polymerization after adding an initiator. At present, there are few reports on polymerizable deep eutectic solvents. [0003] Highly transparent, stretchable, conductive, and highly biocompatible elastomer materials have broad de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F226/06C08F222/38C08F222/20C08F222/28C08F222/14C08F2/48
CPCC08F226/06C08F222/1063C08F2/48C08F222/385C08F222/28C08F222/104Y02P20/54
Inventor 陈明清杜德焰施冬健东为富倪忠斌
Owner JIANGNAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products