Hemostatic composite hydrogel as well as preparation method and application thereof

A composite hydrogel and hydrogel technology, applied in applications, medical formulations, surgical adhesives, etc., can solve problems such as ineffective release, insufficient hemostasis, and inability to seal wounds in time, achieving good biological safety , The preparation process is controllable and the preparation process is simple

Active Publication Date: 2022-04-22
INST OF MEDICINE & HEALTH GUANGDONG ACAD OF SCI
View PDF15 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the instability of the thrombin aqueous solution at room temperature, it brings a lot of inconvenience to clinical application.
[0003] The existing hemostatic materials have the following problems: due to the poor adhesion between the hemostatic material and the bleeding wound, the hemostatic material cannot be stably wrapped in the base material, resulting in hemostasis failure, or the dispersion effect of the hemostatic material in the base material is not good and cannot Effective release, unable to seal the wound in time, so the hemostasis is not fast enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hemostatic composite hydrogel as well as preparation method and application thereof
  • Hemostatic composite hydrogel as well as preparation method and application thereof
  • Hemostatic composite hydrogel as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] This embodiment prepared a hemostatic composite hydrogel, the specific process is:

[0038] (1) Take 2.5g of bovine serum albumin and dissolve it in 10mL of aqueous solution to prepare a bovine serum albumin aqueous solution with a mass concentration of 25%, stir evenly at room temperature, add 0.625g of methacrylated gelatin, and heat to 50°C. Stir to dissolve evenly;

[0039] (2) Cool to 37° C., take 200 μL of the cooled solution, and add 10 μL of thrombin solution with a concentration of 100 U / mL.

[0040] (3) Vortex, mix evenly, and cool at room temperature for 15 minutes to shape.

Embodiment 2

[0042] This embodiment prepared a hemostatic composite hydrogel, the specific process is:

[0043] (1) Take 2.5g of bovine serum albumin and dissolve it in 10mL of aqueous solution to prepare a bovine serum albumin aqueous solution with a mass concentration of 25%, stir evenly at room temperature, add 0.625g of methacrylated gelatin, and heat to 50°C. Stir to dissolve evenly;

[0044] (2) Cool to 37° C., take 200 μL of the cooled solution, and add 5 μL of thrombin solution with a concentration of 100 U / mL.

[0045] (3) Vortex, mix evenly, and cool at room temperature for 15 minutes to shape.

Embodiment 3

[0047] This embodiment prepared a hemostatic composite hydrogel, the specific process is:

[0048] (1) Take 2.5g of bovine serum albumin and dissolve it in 10mL of aqueous solution to prepare a bovine serum albumin aqueous solution with a mass concentration of 25%, stir evenly at room temperature, add 0.625g of methacrylated gelatin, and heat to 50°C. Stir to dissolve evenly;

[0049] (2) Cool to 37° C., take 200 μL of the cooled solution, and add 2 μL of thrombin solution with a concentration of 100 U / mL.

[0050] (3) Vortex, mix evenly, and cool at room temperature for 15 minutes to shape.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

According to the hemostatic composite hydrogel and the preparation method and application thereof, the hemostatic composite hydrogel is crosslinked through physical action to form a network, thrombin is wrapped in the physical network, when water is added for dilution or the hemostatic composite hydrogel is applied to wound blood for dilution, the wrapped thrombin can be released, and rapid hemostasis of the wound is achieved. The hemostatic composite hydrogel disclosed by the invention is strong in mechanical property and good in biological safety. The preparation raw materials are wide in source, the preparation process is simple, the preparation process is controllable, and large-scale production can be realized.

Description

technical field [0001] The invention belongs to the field of hydrogels, in particular to a hemostatic composite hydrogel and its preparation method and application. Background technique [0002] Thrombin is a clinically used hemostatic drug, mainly used for hemostasis in trauma, surgery, etc. Thrombin acts on the last step of the blood coagulation process to promote the conversion of soluble fibrinogen in the plasma into insoluble fibrin to achieve the purpose of quick hemostasis. However, because the thrombin aqueous solution is unstable at room temperature, it brings a lot of inconvenience to clinical application. [0003] The existing hemostatic materials have the following problems: due to the poor adhesion between the hemostatic material and the bleeding wound, the hemostatic material cannot be stably wrapped in the base material, resulting in hemostasis failure, or the dispersion effect of the hemostatic material in the base material is not good and cannot Effective ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61L24/00A61L24/10C08J3/075C08J3/24C08L89/00
CPCA61L24/0031A61L24/0015A61L24/001A61L24/043C08J3/075C08J3/246A61L2400/04A61L2300/254A61L2300/418A61L2300/602C08J2389/00C08J2489/00C08L89/00
Inventor 国翠平于珊高博韬黄骏
Owner INST OF MEDICINE & HEALTH GUANGDONG ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com