Antibacterial full-degradable plastic material based on Chinese herbal medicine extract and preparation method of antibacterial full-degradable plastic material

A technology of plastic materials and Chinese herbal medicine, which is applied in the field of antibacterial fully degradable plastic materials and their preparation, can solve the problems of limited antibacterial performance and difficult degradation of plastic materials, and achieve the effect of being conducive to industrial production and use, cheap, and cheap in the market

Pending Publication Date: 2022-05-13
YINGKOU DONGSHENG IND +1
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a kind of antibacterial fully degradable plastic material based on Chinese herbal medicine extract and its preparation method, to solve the problems of limited bacteriostatic performance and difficult degradation of plastic materials in the current market proposed by the above-mentioned background technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial full-degradable plastic material based on Chinese herbal medicine extract and preparation method of antibacterial full-degradable plastic material
  • Antibacterial full-degradable plastic material based on Chinese herbal medicine extract and preparation method of antibacterial full-degradable plastic material
  • Antibacterial full-degradable plastic material based on Chinese herbal medicine extract and preparation method of antibacterial full-degradable plastic material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] A method for preparing an antibacterial fully degradable plastic material based on extracts of Chinese herbal medicines, comprising the following steps;

[0033] Step 1: crush the leaves of mugwort and pomegranate peels separately, pass through a 2-mesh sieve, and mix according to a certain mass ratio to obtain a compound Chinese herbal medicine powder, wherein the leaves of mugwort account for 50-90% and the peel of pomegranates accounts for 10-50%;

[0034] Step 2: Add the compound Chinese herbal medicine powder in step 1 into tap water according to the mass (Kg) volume (L) ratio of 1:5-1:20, mix evenly, and stir and extract at 100°C for 20-90 minutes;

[0035] Step 3: centrifuging the extract in step 2 to obtain the extract supernatant;

[0036] Step 4: Mix and stir PBAT particles with 0.5-2% coupling agent, 0.5-2% solubilizer, 0.5-2% heat stabilizer, and 0.01-0.2% antioxidant to obtain PBAT mixed material liquid, and The supernatant of step 3 is added to the PBAT mix...

Embodiment 1

[0045] Step 1: crush the leaves of mugwort and pomegranate peels separately, pass through a 2-mesh sieve, mix the leaves of mugwort and the peels of pomegranate according to a certain mass ratio, and obtain a compound Chinese herbal medicine powder, wherein the leaves of mugwort account for 90%, and the peel of pomegranates accounts for 10%;

[0046] Step 2: Add the compound Chinese herbal medicine powder in step 1 into tap water according to the mass (Kg) volume (L) ratio of 1:20, mix well, and stir and extract at 100°C for 60 minutes;

[0047] Step 3: centrifuging the extract in step 2 to obtain the extract supernatant;

[0048] Step 4: Mix and stir the PBAT particles with 1% coupling agent, 1% solubilizer, 1% heat stabilizer, and 0.1% antioxidant to obtain the PBAT mixed material liquid, and prepare the supernatant of step 3 according to 20 The mass (Kg) ratio of % joins in the PBAT mixed material liquid, continues high-speed mixing and stirring;

[0049] Step 5: drying th...

Embodiment 2

[0053] Step 1: crush the leaves of mugwort and pomegranate peels separately, pass through a 2-mesh sieve, and mix according to a certain mass ratio to obtain a compound Chinese herbal medicine powder, wherein the leaves of mugwort account for 70% and the peel of pomegranates accounts for 30%;

[0054] Step 2: Add the compound Chinese herbal medicine powder in step 1 into tap water according to the mass (Kg) volume (L) ratio of 1:10, mix evenly, and stir and extract at 100°C for 40 minutes;

[0055] Step 3: centrifuging the extract in step 2 to obtain the extract supernatant;

[0056] Step 4: Mix and stir the PBAT particles with 1.5% coupling agent, 1.5% solubilizer, 1.5% heat stabilizer, and 0.05% antioxidant to obtain the PBAT mixed material liquid, and prepare the supernatant of step 3 according to 10 Add the mass (Kg) ratio of %-40% into the PBAT mixture liquid, and continue to mix and stir at a high speed;

[0057] Step 5: drying the PBAT mixture containing Chinese herbal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an antibacterial full-degradable plastic material based on a Chinese herbal medicine extract. The antibacterial full-degradable plastic material comprises the following components: folium artemisiae argyi, pomegranate rind, PBAT, PLA, a coupling agent aluminate, a solubilizer stearic acid, a heat stabilizer epoxidized soybean oil and an antioxidant 1010. The preparation method comprises the following steps: respectively crushing and mixing folium artemisiae argyi and pomegranate rind, adding tap water, uniformly mixing, extracting supernatant liquid, adding the supernatant liquid into PBAT mixed material liquid, continuously mixing and stirring at a high speed, and then drying to obtain the master batch. According to the antibacterial full-degradable plastic material based on the Chinese herbal medicine extract, folium artemisiae argyi and pomegranate rind are used as Chinese herbal medicine components, the Chinese herbal medicine extract is obtained through high-temperature water extraction, the extract and a PBAT component are mixed, the extract is loaded and distributed into a PBAT material by means of mixing distribution and high-temperature protection effects of a coupling agent, a solubilizer and a protective agent, and the antibacterial full-degradable plastic material based on the Chinese herbal medicine extract is obtained. And further mixing with a PBAT / PLA composite material to prepare the antibacterial plastic material which contains Chinese herbal medicine components, has an antibacterial function and can be completely degraded in the environment.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to an antibacterial fully degradable plastic material based on extracts of Chinese herbal medicines and a preparation method thereof. Background technique [0002] With the continuous improvement of people's demand for food quality, safety and hygiene and the advocacy of green packaging concepts, antibacterial materials have been widely used in food packaging. Antibacterial materials are a general term for new functional materials that have antibacterial and bactericidal properties and antagonize microorganisms. By adding or compounding one or several specific antibacterial components (antibacterial agents) to ordinary materials, the antibacterial properties of materials are obtained and enhanced. . Antibacterial plastic is the fastest growing, highest premium and most widely used packaging material among antibacterial materials. When ordinary plastics are endowed with a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L67/04C08L91/00C08K5/00C08K5/10C08K5/09C08K5/134C08J5/18B65D65/46
CPCC08J5/18B65D65/466C08J2367/02C08J2367/04C08J2467/02C08J2467/04C08K5/0058C08K5/10C08K5/09C08K5/1345
Inventor 文博李姝谊郝天禹徐卫平任传鉴黄程程张守玉金宁
Owner YINGKOU DONGSHENG IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap