High-modulus high-toughness cycloolefin copolymer material and preparation method thereof

A cyclic olefin copolymer and high toughness technology, applied in the field of high-modulus and high-toughness cyclic olefin copolymer materials and their preparation, can solve the problems of loss of COC high transparency, low rigidity and toughness, and restrictions, and achieve improved rigidity, small size, etc. Effects of dispersion size and distribution, high stiffness and toughness

Pending Publication Date: 2022-07-29
KINGFA SCI & TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the present stage, the research on COC basically focuses on the synthesis of COC and the modification of new pure COC. For PCR-grade COC materials, because they are usually co-extruded with LLDPE films, it is difficult to separate them by infrared and NMR during recycling. The high transparency of COC and the presence of LLDPE lead to low rigidity and toughness of PCR-grade COC materials, which limits the application of PCR-grade COC materials, and there is basically no research on its modification.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-modulus high-toughness cycloolefin copolymer material and preparation method thereof
  • High-modulus high-toughness cycloolefin copolymer material and preparation method thereof
  • High-modulus high-toughness cycloolefin copolymer material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The present invention will be further described below in conjunction with specific embodiments. It should be understood that these examples are only used to illustrate the present invention and not to limit the scope of the present invention. In addition, it should be understood that after reading the content taught by the present invention, those skilled in the art can make various changes or modifications to the present invention, and these equivalent forms also fall within the scope defined by the appended claims of the present application.

[0020] The reagents, methods and equipment used in the present invention, unless otherwise specified, are conventional reagents, methods and equipment in the technical field.

[0021] The raw materials used in the following examples and comparative examples are as follows:

[0022] Cyclic Olefin Copolymer 1#: UP-66 (LW), 260℃, 2.16kg melt index is 5g / 10min, the mass content of COC is 85%-90%, purchased from Japan Appleitz;

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a high-modulus and high-toughness cycloolefin copolymer material and a preparation method thereof. The high-modulus and high-toughness cycloolefin copolymer material comprises a PCR (Polymerase Chain Reaction)-grade cycloolefin copolymer, a thermoplastic elastomer, talcum powder and a processing aid. The cycloolefin copolymer disclosed by the invention has relatively high rigidity and toughness and also has excellent chemical resistance; and meanwhile, the preparation of the material also conforms to the current concept of environmental protection.

Description

technical field [0001] The invention belongs to the field of polymer materials, in particular to a high-modulus and high-toughness cyclic olefin copolymer material and a preparation method thereof. Background technique [0002] Cyclo-Olefin Copolymer (COC for short) is a thermoplastic amorphous transparent polymer material obtained by copolymerizing cycloolefin monomer and α-olefin. Generally speaking, cyclic olefin copolymer refers to the copolymer of cyclic olefin and ethylene, which is prepared by Ziegler-Natta and metallocene catalyzed polymerization. Compared with traditional polyolefin materials such as polyethylene and polypropylene, cyclic olefin copolymer has unique and excellent properties, such as excellent optical properties, its light transmittance can reach 91%, and it has low birefringence and High ampere number, low dielectric constant and dielectric loss, good dimensional stability and high strength, widely used in optical devices, packaging, medical and el...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L45/00C08L53/02C08K3/34
CPCC08L45/00C08L53/025C08K3/34
Inventor 李栋栋陈平绪叶南飚杨霄云陆湛泉王爱东赵治国姜向新
Owner KINGFA SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products