Method for making ammonium polyphosphate clad by microcapsules

A technology of coating ammonium polyphosphate and ammonium polyphosphate, which is applied in the direction of microcapsule preparation, microsphere preparation, etc., can solve the problems of reduced yield of coated APP, environmental pollution, particle size change, etc.

Inactive Publication Date: 2005-08-31
SHANGHAI RES INST OF CHEM IND
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this method solves the shortcomings of agglomeration on the wall of the reactor and obvious change in particle size of coated APP, some APP will be hydrolyzed during the coating process, resulting in a decrease in the yield of coated APP.
In addition, the free formaldehyde content in the coated product reaches 5.0-8.0mg / 100g, so when used as a flame retardant, there is concern about causing environmental pollution
Another problem is that polymer products mixed with such coated APP materials as flame retardants cannot be used for long-term contact with water, especially for occasions where they are in contact with water at high temperatures, mainly because of the It still contains a small amount of uncoated components, which will be lost by water dissolution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] In a reactor with a stirring and reflux device, add 180ml of ethanol and 100g of APP, heat to 80°C under stirring, then put in 28g of melamine-formaldehyde prepolymer, and then put in 2.0% ammonium chloride by weight of the prepolymer, Stir and react for about 30 minutes to harden the resin. Then lower the temperature of the kettle to about 50°C, add urea equivalent to 1.0% of the weight of the solid reactant, continue to stir, react for about 30 minutes, cool, filter, and dry the filter cake at 90°C and 30mmHg to obtain a free-flowing Coated APP 115.5g.

Embodiment 2

[0040] In a reaction kettle with a stirring and reflux device, add 180ml of ethanol and 100g APP, and at a temperature of 80°C, add 35g of melamine-formaldehyde prepolymer, and add 3.0% ammonium chloride by weight of the prepolymer, stir, React for 60 minutes to harden the resin. Then lower the temperature of the kettle to about 50°C, then add 3.0% urea equivalent to the weight of the solid reactant, continue to stir and react for about 20 minutes, cool and filter, and dry the filter cake at 90°C and 30mmHg to obtain a liquid with good fluidity. White coated APP 112.6g.

Embodiment 3

[0042] Feeding intake and operation are all carried out by embodiment 1, but the add-on of prepolymer is 17g, and the add-on of ammonium chloride is 2% of prepolymer weight, and the add-on of urea is 1% of solid reactant weight, and reaction finishes After cooling and filtering, the filter cake was dried at 90° C. and 30 mmHg to obtain 105.8 g of white coated APP with good free-flowing properties.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A microsoftgel coated ammonium polyphosphate is prepared through suspending the ammonium polyphosphate particles in disperser, adding melamine, formaldehyde and hardening agent at 60-150 deg.C, stirring while reaction, adding formaldehyde capture, stirring while reacting at 30-60 deg.C for 10-30 min, filtering and drying. It can be used as flame-retarding agent.

Description

technical field [0001] The invention relates to the technology of using ammonium polyphosphate as the core material and coating with microcapsules, especially the coating technology of using melamine-formaldehyde resin as the capsule wall material. Background technique [0002] Ammonium polyphosphate (ammonium polyphosphate, hereinafter referred to as APP) has the following general structural formula: [0003] (NH 4 ) n+2 P n o 3n+1 (where n is an integer from 20 to 800) [0004] It is usually a fluid powdery object, close to neutral, good chemical stability, safe to use, and can be mixed with other substances without causing chemical changes; its high content of phosphorus and nitrogen can produce P-N synergistic effect, so It is an efficient inorganic flame retardant. [0005] However, since APP is a kind of hydrophilic powder, it will absorb moisture in the air when it is stored in the air, resulting in the aggregation state of APP. 2 o 5 Hydrolysis, moreove...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J13/02C08K9/10C08L75/04C09K21/12C09K21/14
Inventor 单渊复於莉莉陈崇伟刘彦明
Owner SHANGHAI RES INST OF CHEM IND