Environment protection type ceramic fibre needling blanket

A technology of ceramic fiber and needle-punched blanket, which is applied in the direction of textiles, papermaking, non-woven fabrics, etc. It can solve the problems of a large amount of dust and particulate matter, and achieve the effect of stable fiber quality, high strength and soft fiber

Inactive Publication Date: 2002-12-18
LUYANG ENERGY SAVING MATERIALS CO LTD
View PDF0 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Traditional ceramic fiber (aluminosilicate ceramic fiber) products, the main component of which is Al 2 o 3 and SiO 2 , the two account for about 97%, and the remaining 3% are potassium, sodium, iron, etc., and the melting temperature is greater than 2000 ° C; due to the production of spinning or blowing methods, coupled with fine fibers (3 ~ 5 μm), resulting in the production process. A lot of dust and particulate matter

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment protection type ceramic fibre needling blanket

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Example 1 Raw material weight ratio: silicon dioxide: aluminum oxide: magnesium oxide = 55:40:4; the raw material is melted at 1700-1900°C, and at 1550-1700°C, it is formed into fibers by blowing or centrifugal spinning process The ceramic fiber is made, the fiber performance is slightly acidic, its pH is about 6.1±, and the non-fibrous matter (slag ball) is less than 8%; after collecting cotton, it is needled into a blanket, and the needled blanket blank passes through 700-900°C The high temperature is shaped into a blanket, and the ceramic fiber needle-punched blanket with soft texture is obtained by cutting. Because the raw material is easy to obtain and its melting temperature is low, the product cost is low, which is beneficial to popularization and application of the product.

[0013] Example

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
thermal resistanceaaaaaaaaaa
Login to view more

Abstract

The present invention belongs to a refractory heat-insulating material, and relates to an environment-protecting ceramic fibre needle-punched carpet and its preparation method. Its raw material silicon dioxide and aluminium oxide are undergone the processes of melting and fibre formation to obtain ceramic fibre, said ceramic fibre is undergone the processes of collecting, needling, heat treatmentand cutting so as to obtain the invented ceramic fibre needle-punched carpet. It is characterized by that its composition also contains 4-6 portions of magnesium oxide and/or calcium oxide, and its fibre-forming process adopts the blowing or centrifugal spinning process. Said fibre is stable in quality and high in yield rate.

Description

technical field [0001] The invention belongs to fire-resistant and heat-insulating materials, and is a high-temperature-resistant inorganic fiber (for example, aluminum silicate ceramic fiber) blanket, in particular to an environment-friendly ceramic fiber needle-punched blanket and a preparation method thereof. The invention is a high-temperature textile fiber that can be used at a temperature of 900-1100°C and has excellent textile performance, and is suitable as a raw material for heat-insulating fiber textiles for equipment and pipelines. Background technique [0002] Traditional ceramic fiber (aluminosilicate ceramic fiber) products, the main component of which is Al 2 o 3 and SiO 2 , the two account for about 97%, and the remaining 3% are potassium, sodium, iron, etc., and the melting temperature is greater than 2000 ° C; due to the production of spinning or blowing methods, and the fine fibers (3 ~ 5 μm), resulting in the production process. Lots of dust and partic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/14D04H1/4209D04H1/46
Inventor 鹿成洪鹿成会王书义李京友杜春刚刘启平
Owner LUYANG ENERGY SAVING MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap