Dry-powder ceramic file adhesive

A tile adhesive and dry powder technology, applied in the field of chemical building materials, can solve the problems of unfavorable environmental protection, high cost of raw materials, unsuitable for wide use, etc., achieve good economic benefits, and be conducive to industrial production and popularization and application, production technology and device simple effect

Inactive Publication Date: 2004-09-15
SHANGHAI UNIV +1
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The raw material cost of the above tile adhesives is relatively expensive, so it is no

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] The present invention and specific embodiment are described in the following:

[0022] chemical composition

[0023] Fineness (residue of 45um square hole sieve): 14%

[0024] Loss on ignition: 4.74%

[0025] Water demand ratio: 98%

[0026] SO 3 Content: 2.23%

[0027] Moisture content: 0.5%

[0028] The present invention is example with preparing 1000 kilograms of dry powder tile adhesives:

[0029] Get 800 kg of secondary fly ash, add it to a specific stirring tank, add 75 kg of activator, 110 kg of Portland cement (mark 42.5), 10 kg of latex powder (fineness is 200 mesh butadiene-styrene Polymer), 4 kg of cellulose ether and 1 kg of defoamer, stirred in a stirring tank for half an hour, after uniform mixing, the dry powder tile adhesive can be obtained.

Example Embodiment

[0030] Embodiment 2: The chemical composition and index of the fly ash utilized in this embodiment are the same as those of the above-mentioned examples. Take the preparation of 1000 kg of dry powder tile adhesive as an example: get 700 kg of fly ash, add it to the stirring tank, and then Add 100 kilograms of calcium sulfate and calcium oxide (weight ratio is 2: 1) mixture, 175 kilograms of Portland cement (marked as 42.5), 20 kilograms of latex powder (fineness is 200 mesh butadiene-styrene polymer) , 4 kg of cellulose ether and 1 kg of defoamer, stirred in a stirring tank for half an hour, so that after uniform mixing, you can get dry powder tile adhesive.

[0031] When using, according to the construction requirements, a certain proportion of water can be added, that is, the dry powder tile adhesive and water are mixed in a ratio of 2:1, and after stirring evenly, it can be used after standing for 10 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a ceramic tile special binder adopting powder coal as main raw material, namely a dry powder ceramic tile binder, its components (wt%): secondary powder coal 60-90%, exciter 3-10%, cement 6-20%, emulsion powder 1-5%, water-retaining agent 0.2-1.0% and defoaming agent 0.05-0.15%. It weighs its components to place in stirring kettle, and uniformly stirs for a period of time to obtain the dry powder ceramic tile binder at once. When used, it is added in a certain proportion of water and uniformly stirred to be used at once. It has better construction property and adhesion or adhesive strength. It develops a new way of synthetical utilization of powder coal.

Description

technical field [0001] The invention relates to a dry powder adhesive for tiles, more specifically, a special adhesive for tiles with fly ash as the main raw material, belonging to the technical field of chemical building materials. Background technique [0002] At present, in the construction and decoration industry, as adhesives for tile paving of building materials, polyvinyl acetal glue plus cement, polymer emulsion with filler, water glass with filler, and polymer materials and Modified powdered product based on cement. Above these ceramic tile adhesives, its raw material cost price is more expensive, should not be widely used, and also unfavorable to environmental protection. Contents of the invention [0003] The purpose of the present invention is to provide a ceramic tile adhesive with fly ash as the main raw material, and open up a new way for the comprehensive utilization of fly ash. [0004] The present invention adopts the following technical solutions to ac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B16/04C04B18/08C04B22/06C04B22/08C04B24/38C04B28/02C09J1/00
CPCC04B28/02
Inventor 陆文雄曹栋樑刘庆赵美丽王超
Owner SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap