Far infrared functional brick and its producing method

A production method, far-infrared technology, applied in light therapy, clay products, and other household appliances, etc., to achieve the effects of maintaining body balance and health, improving physical fitness, and enhancing immunity

Inactive Publication Date: 2004-11-17
陈民全
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the floor tiles and wall tiles used at home and abroad are made of marble, imitation marble, terrazzo or porcelain products. Most of them are produced by radiation and other radiation in use, and will not produce the effect of purifying the air and generating negative ions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] Get 31.5 kilograms of raw material silicon trioxide, 7 kilograms of aluminum oxide, 0.5 kilograms of potassium oxide, 2 kilograms of ferric oxide, 1.5 kilograms of boron trioxide, 0.5 kilograms of sodium oxide, and 50 kilograms of clay for crushing; After the particle size is about 0.03 mm, it is fully mixed, and water is added and stirred to make a brick, which is placed in a kiln, fired at 1000 ° C for 8 hours, and taken out to be the finished product.

Embodiment 2

[0010] Take 32.5 kg of raw material silicon trioxide, 7.8 kg of aluminum oxide, 0.8 kg of potassium oxide, 2.3 kg of ferric oxide, 2.3 kg of diboron trioxide, 1 kg of sodium oxide, and 53.5 kg of clay for crushing; The particle size is about 0.03 mm. After fully mixing, add water and stir well to make bricks, put them in the kiln, and burn them at 1250 ° C for 8 hours to take out the finished products.

Embodiment 3

[0012] Get 33.5 kilograms of raw material silicon trioxide, 8.5 kilograms of aluminum oxide, 1 kilogram of potassium oxide, 2.5 kilograms of ferric oxide, 3 kilograms of diboron trioxide, 1.5 kilograms of sodium oxide, and 57 kilograms of clay for crushing; The particle size is about 0.03 mm. After fully mixing, add water and stir well to make bricks, put them in a kiln, and burn them at 1500 ° C for 8 hours to take out the finished products.

[0013] The above-mentioned components are generally present in the raw materials of tourmaline, and the main components in the tourmaline can be tested for material selection. Other trace mineral elements contained in the tourmaline can be ignored. Bricks, floor tiles and other building products will have the characteristics of generating negative ions and no radiation after being tested. In addition, the natural tourmaline with the above-mentioned components can also be directly used as a building material with good strength and good p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Mohs hardnessaaaaaaaaaa
Login to view more

Abstract

The invention relates to building material such as ground tile and wall tile capable of producing negative ions and being radioactive-ray-free and process for its preparation, the tiles comprise the components of (by weight percentage) silicon dioxide 31.5%-33.5%, aluminum oxide 7.0%-8.5%, potassium oxide 0.5%-1.0%, ferric oxide 2.0%-2.5%, diboron trioxide 1.5%-3%, sodium oxide 0.5%-1.5%, pottery clay 50%-57%. The preparation process comprises the steps of, disintegrating the raw material to grain size of 0.03 mm, watering and stirring, immersing, making blank, burning 8 hours at 1000 deg. C to 1500 deg. C.

Description

Technical field: [0001] The invention relates to a construction engineering material, in particular to a construction material such as floor tiles and wall tiles that can generate negative ions and no radiation, and a manufacturing method thereof. Background technique: [0002] Silicate minerals, also known as tourmaline. Its main components contain Na, Fe, Mn, Al, Li, B, Si and other elements, and its molecular expression is X 1 Y 9 B 3 Si 6 (OH·F) 4 , X represents one or more elements in Ca, Na, K, Mn, Y represents one or more elements in Mg, Fe, Al, Cr, Ti, Li, Mohs hardness 7~7.5, This substance has been developed and utilized in many fields such as water activation, sewage treatment, air purification, washing, fertilizer and so on. Japanese Patent No. JP2000139207 reports the use of this material as a fertilizer. At present, there is no data record that the tourmaline is used for building floor tiles and wall tiles. At present, the floor tiles and wall tiles use...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61L9/22A61N5/06C04B33/02C04B33/13E04C1/00
Inventor 陈民全
Owner 陈民全
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap