Far infrared functional brick and its producing method

A production method, far-infrared technology, applied in the direction of light therapy, clay products, other household appliances, etc., to achieve smooth metabolism, maintain body balance and health, and recover from fatigue.

Inactive Publication Date: 2005-12-07
陈民全
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the floor tiles and wall tiles used at home and abroad are made of marble, imitation marble, terrazzo or porcelain products. Most of them are produced by radiation and other radiation in use, and will not produce the effect of purifying the air and generating negative ions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] Take 31.5 kg of raw materials silicon trioxide, 7 kg of aluminum oxide, 0.5 kg of potassium oxide, 2 kg of ferric oxide, 1.5 kg of diboron trioxide, 0.5 kg of sodium oxide, and 50 kg of pottery clay for crushing; fine powder processing to After the particle size is about 0.03 mm, mix it well, add water and stir well to make bricks, put them in the kiln, and fire them at 1000°C for 8 hours, then take them out to be the finished product.

Embodiment 2

[0010] Get 32.5 kilograms of raw material silicon trioxide, 7.8 kilograms of aluminum oxide, 0.8 kilogram of potassium oxide, 2.3 kilograms of ferric oxide, 2.3 kilograms of diboron trioxide, 1 kilogram of sodium oxide, and 53.5 kilograms of clay for crushing; The particle size is about 0.03 mm. After fully mixing, add water and stir evenly to make adobe, put it in the kiln, and fire it at 1250 ° C for 8 hours. After taking it out, it is the finished product.

Embodiment 3

[0012] Get 33.5 kilograms of raw material silicon trioxide, 8.5 kilograms of aluminum oxide, 1 kilogram of potassium oxide, 2.5 kilograms of ferric oxide, 3 kilograms of diboron trioxide, 1.5 kilograms of sodium oxide, and 57 kilograms of clay for crushing; The particle size is about 0.03 mm. After fully mixing, add water and stir evenly to make bricks, put them in a kiln, and fire them at 1500 ° C for 8 hours. After taking them out, they are finished products.

[0013] The above-mentioned ingredients are commonly found in tourmaline raw materials, and the main ingredients in tourmaline can be tested for material selection. Other trace mineral elements contained in tourmaline can be ignored. In this way, the wall made according to the above formula and production method after material selection Building products such as bricks and floor tiles will have the characteristics of generating negative ions and no radiation after being tested. In addition, natural tourmaline with good...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Mohs hardnessaaaaaaaaaa
Login to view more

Abstract

The invention relates to building material such as ground tile and wall tile capable of producing negative ions and being radioactive-ray-free and process for its preparation, the tiles comprise the components of (by weight percentage) silicon dioxide 31.5%-33.5%, aluminum oxide 7.0%-8.5%, potassium oxide 0.5%-1.0%, ferric oxide 2.0%-2.5%, diboron trioxide 1.5%-3%, sodium oxide 0.5%-1.5%, pottery clay 50%-57%. The preparation process comprises the steps of, disintegrating the raw material to grain size of 0.03 mm, watering and stirring, immersing, making blank, burning 8 hours at 1000 deg. C to 1500 deg. C.

Description

Technical field: [0001] The invention relates to a building engineering material, in particular to building materials such as floor tiles and wall tiles capable of generating negative ions and without radiation, and a manufacturing method thereof. Background technique: [0002] Silicate minerals, also known as tourmaline. Its main components contain Na, Fe, Mn, Al, Li, B, Si and other elements, and its molecular expression is X 1 Y 9 B 3 Si 6 (OH·F) 4 , X represents one or more elements of Ca, Na, K, Mn, Y represents one or more elements of Mg, Fe, Al, Cr, Ti, Li, Mohs hardness 7-7.5, This substance has been developed and utilized in many fields such as water activation, sewage treatment, air purification, washing, and fertilizer. Japanese Patent No. JP2000139207 reports that this material is used as a fertilizer. At present, there is no information documenting the use of tourmaline on floor tiles and wall tiles for construction. At present, floor tiles and wall tile...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A61L9/22A61N5/06C04B33/02C04B33/13E04C1/00
Inventor 陈民全
Owner 陈民全
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap