Molding composition based on polyetheramides
一种模制组合物、聚醚酰胺的技术,应用在管状物品、应用、家里用具等方向,能够解决不适于生产、达不到稳定性等问题
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment Construction
[0048] Preparation of polyetheramide:
[0049] A 200 L agitated autoclave was loaded with the following starting reaction materials:
[0050] 26.11kg 75% 1,6-hexanediamine aqueous solution,
[0051] 52.94kg of 1.12-dodecanedioic acid,
[0052] 25.55kg of JEFFAMIN D400 and
[0053] 100g of 50% aqueous solution of hypophosphorous acid.
[0054] The starting materials were melted under a nitrogen atmosphere and heated and stirred in a sealed autoclave to about 220° C. while adjusting the internal pressure to about 20 bar. This pressure was maintained for 2 hours, after which the melt was reheated to 230°C with continuous depressurization to atmospheric pressure, and this temperature was maintained for 1.5 hours under nitrogen flow. The vessel was then evacuated to 28 mbar over a period of 3 hours and maintained at this pressure for a further 3 hours until torque indicated that the viscosity of the melt had ceased to rise. Then use the gear pump to release the melt and gr...
PUM
Property | Measurement | Unit |
---|---|---|
melting point | aaaaa | aaaaa |
melting point | aaaaa | aaaaa |
melting point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap