Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Thermoplastic elastomer material and its preparation method

A thermoplastic elastomer and raw material technology, applied in the field of thermoplastic elastomer materials, can solve the problems of easy slipping and falling off, ABS and rubber two-phase incompatibility, weak bonding, etc., achieve good bonding effect and prolong service life Effect

Inactive Publication Date: 2006-05-03
SHANGHAI SUNNY
View PDF0 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to improve the feel of handles and toy products, a layer of rubber is often used to cover the surface, but because the two phases of ABS and rubber are incompatible, the rubber is simply covered on the surface, the bond is not firm, and it is easy to slip and fall off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1 and 2

[0037] Put all the raw materials in proportion into a high mixer and mix them for 4 minutes, discharge, and then use a screw extruder to extrude and granulate. The processing temperature is 180°C, and the screw speed is 200 rpm.

[0038] Sample 1, sample 2 made according to embodiment 1, embodiment 2 and AES company santoprene series 101-55 product performance contrast

[0039] project

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
degree of graftingaaaaaaaaaa
Login to View More

Abstract

The invention relates to a thermoplastic elastomer material, which comprises: SEBS-A 10-40%, SEBS-B 10-40%, plasticizer 20-50%, TPU 5-15%, solvent 1-8%, anti-oxidant 0.1-0.5%, and inorganic mineral 1-10%. Wherein, the preparation method comprises: selecting materials to put into strong-mixing machine for 2-5min; out feeding; extruding and granulating in the screw machine with 180-600r / min rotation speed at 160-240Deg. This invention changes the polarity of TPE, obtains well sticking effect, and has no harm to environment and human.

Description

technical field [0001] The invention relates to a thermoplastic elastomer material and a preparation method thereof, in particular to a modified transparent TPE material that can be bonded to ABS in secondary injection molding, and can be used for injection molding various handles and toy products, belonging to thermoplastic elastomer materials technology field. Background technique [0002] ABS resin is widely used in various handles and toy products due to its good fluidity, rigidity, chemical resistance, and gloss. In order to improve the feel of handles and toy products, a layer of rubber is often used to coat the surface. However, due to the two-phase incompatibility of ABS and rubber, the rubber is simply covered on the surface, and the bond is not firm, and it is easy to slip and fall off. Contents of the invention [0003] The object of the present invention is to provide a thermoplastic elastomer material that can be bonded to ABS in secondary injection molding a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L53/02B29C48/395C08K5/524
CPCB29C48/022B29C2948/92561B29C2948/9259B29C2948/92704
Inventor 辛敏琦陈晓东杨涛唐倬吴小龙
Owner SHANGHAI SUNNY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com