A surface treatment and mechanical steel technology, applied in the direction of metal material coating process, coating, solid-state diffusion coating, etc., can solve the problem that low-carbon alloy steel is expensive, and the corrosion resistance and fatigue resistance of steel rings are not greatly improved. Improvement, high cost and other issues
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0008] A surface treatment method for the steel ring of a worsted spinning machine, comprising the following steps: subjecting the gold-processed steel to carbonitriding heat treatment, then polishing and cleaning, and then putting it into a nitriding furnace for ion nitriding treatment, nitriding The treated steel is firstly polished, then cleaned and degreased, and then put into the air furnace for preheating. The preheating temperature is 350℃~400℃, and the preheating time is 20~40 minutes. Oxidation in an oxidation furnace, the oxidation temperature is 350°C to 450°C, and the oxidation time is 30 to 40 minutes. Put the oxidized steel ring in the water tank to desalt and clean it, then dry it, and then get the finished product after oil immersion or oil injection.
[0009] The main function of preheating is to dry the moisture on the surface of the workpiece, so that the cold workpiece can be heated up before entering the oxidation furnace, so as to prevent the salt bath sp...
Embodiment 2
[0029] A surface treatment method for a steel ring of a worsted spinning machine, comprising the following steps: subjecting the gold-processed steel to carbonitriding heat treatment, then polishing and cleaning, and then putting it into a nitriding furnace for salt bath nitriding, nitriding The treated steel is firstly polished, then cleaned and degreased, and then put into the air furnace for preheating, the preheating temperature is 350°C ~ 400°C, and the preheating time is 20 minutes, and then the preheated steel ring is put into the oxidation furnace Medium oxidation, the oxidation temperature is 450°C, and the oxidation time is 40 minutes. Put the oxidized steel ring in the water tank to desalt and clean it, then dry it, and then get the finished product after oil immersion or oil injection.
Embodiment 3
[0031] A surface treatment method for a steel ring of a worsted spinning machine, comprising the following steps: subjecting the gold-processed steel lead to carbonitriding heat treatment, then polishing and cleaning, and then putting it into a nitriding furnace for gas soft nitriding treatment, nitrogen The chemically treated steel is first polished, then cleaned and degreased, and then put into an air furnace for preheating. The preheating temperature is 350°C to 400°C, and the preheating time is 40 minutes. Oxidation in a furnace, the oxidation temperature is 380°C, and the oxidation time is 35 minutes. Put the oxidized steel ring in the water tank to desalt and clean it, then dry it, and then get the finished product after oil immersion or oil injection.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap