Heterogeneous metal joining member excellent in corrosion resistance and process for preparing same

A technology for dissimilar metals and joining components, applied in metal material coating process, liquid chemical plating, coating and other directions, can solve the problems of components that cannot be applied to complex shapes, environmental problems, manufacturing difficulties, etc., to improve the resistance to dissimilar metals. Contact Corrosive Effects

Inactive Publication Date: 2006-11-22
KOBE STEEL LTD
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Conventional technology 1 cannot be applied to components with complex shapes because it uses thermal spraying
Conventional techniques 2, 4 and 8 are difficult to paint at the closest position or gap of the joint
Conventional Technology 3 It is difficult to implement the operation of stably applying DC voltage by providing terminals on different metal materials for conveyors or building materials
Conventional Technology 5 The operation of applying Cr plating to metals has limitations in the size of applicable members
Also, since hexavalent chromium is used, there are environmental concerns
Conventional Technology 6: It is very difficult to manufacture a thin piece plated with dissimilar metals in the junction, and there is a possibility that the thinner piece will disappear due to the heat at the time of joining.
Conventional technology 7, when applied to joint members, has little effect because the plating film at the joint part is melted and removed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heterogeneous metal joining member excellent in corrosion resistance and process for preparing same
  • Heterogeneous metal joining member excellent in corrosion resistance and process for preparing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0051] 1. Experimental method

[0052] (1) spot welding

[0053] The soft steel plate (30×100×0.8mm) and the aluminum plate (6022 and 5023, 30×100×0.8mm) were spot welded under the conditions of 12kV and 200ms.

[0054] (2) Zinc salt treatment

[0055] It was immersed in the solution shown in Table 1 at 60 degreeC for 30-120 s.

[0056] (3) Chemical conversion treatment

[0057] Treatment process: follow (a) degreasing → (b) water washing → (c) surface adjustment → (d) chemical conversion treatment (dipping treatment) → (e) drying after chemical conversion → (f) water washing → (g) pure water washing → (h ) Dehydration and drying → (i) The order of coating was processed.

[0058] (a) Degreasing: using an alkaline degreasing treatment agent (manufactured by Nippon Paint Co., Ltd., trade name "Sufficrina-SD250", A agent: 1.5wt%, B agent: 0.9wt% aqueous solution, dipped at 43°C Processed for 2 minutes.

[0059] (b) Washing with water: The sample was immersed in channel wate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a heterogenic metal joint structure preparing method with excellent corrosion resistance, which is characterized by the following: immersing the butt iron material and aluminum or aluminum alloy structure in the solution with fluorine coordination and zinc ion; evolving near the butt part for metal zinc; improving touching corrosion-resistance of heterogenic metal reliably.

Description

technical field [0001] The present invention relates to a member excellent in dissimilar metal contact corrosion resistance used in aluminum-steel dissimilar metal joints used in automobiles and the like, and to a manufacturing method thereof. Background technique [0002] It is known that when dissimilar metals are used in combination in joints of components such as automobiles, corrosion is promoted because the dissimilar metals come into contact with each other to conduct electricity. [0003] The corrosion caused by the contact of such dissimilar metals is caused by the difference in the ionization tendency of the metals, a potential difference is generated between the metals, and a corrosion current flows. Conventionally, the following countermeasures have been known to prevent corrosion caused by contact of dissimilar metals. [0004] (1) Conventional technology 1 (patent document 1 etc.) [0005] When the metal exhibiting a low potential is in contact with the metal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C18/16C23F15/00
Inventor 井户秀和武田实佳子漆原亘加藤淳
Owner KOBE STEEL LTD