A blue magnetic optical disk

A technology of optical disc and blue light, applied in the direction of magnetic recording, magnetic recording, beam reproduction, etc., can solve the problem of reducing the Kerr effect, and achieve the effect of improving the structure, good thermal conductivity, and improving the signal-to-noise ratio

Inactive Publication Date: 2010-09-15
SHANGHAI INST OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the increase of the readout laser power will cause the temperature in the focused spot to be too high, which will further reduce the Kerr effect. How to keep the temperature of the recording layer from rising too high under the action of high-power focused blue light is the optimal design of TbFeCo Blu-ray magneto-optical discs key

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A blue magnetic optical disk
  • A blue magnetic optical disk
  • A blue magnetic optical disk

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] against Figure 1b The structure of the Blu-ray magneto-optical disk of the present invention shown in , firstly, the thickness of each film layer must be determined. According to the optimal design of the film system based on the optical feature matrix, a group of film thicknesses are obtained as follows: the first dielectric layer is 30nm, the recording layer is 25nm, the thermal control layer is 10nm, the second dielectric layer is 50nm, and the reflective layer is 100nm. At this time, the Kerr angle of the film system is 0.7255 degrees, and the reflectivity is 20.29%. When optimizing the design, the laser wavelength is 410nm, which is the wavelength of blue light. In addition to the thermal control layer, Figure 1a The traditional magneto-optical disk shown and the blue-ray magneto-optical disk of the present invention have the same film thickness parameters, and the thermal properties of the two magneto-optical disk structures are compared at this time. figure ...

Embodiment 2

[0021] Four-layer and five-layer film samples were prepared by SPF-430H magnetron sputtering system. The film thickness of each film layer is the same as embodiment 1. The ultimate vacuum of the sputtering system can reach 7×10 -5 Pa, using Ar gas as sputtering gas, N 2 As the SiN reactive sputtering gas, the sputtering power is 400kV, and the sputtering pressure is 2Pa. Glass is used as the substrate material, and its size is Φ2cm. For thin film samples with four-layer and five-layer structures prepared by sputtering, a focused spot Kerr effect test device is used, such as Figure 5 As shown, the temperature effect is investigated, and the laser is incident from the substrate layer during the measurement. due to Tb 22 (Fe 85 co 15 ) 78 The compensation temperature of the film is less than room temperature, so when the laser is irradiated, the temperature of the film increases and its coercive force decreases. When close to the Curie temperature, the coercive force is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Curie pointaaaaaaaaaa
coercivityaaaaaaaaaa
Login to view more

Abstract

This invention discloses one blue light magnetic disc, which comprises underlay, first SiN media layer, TbFeCo record layer, second SiN media layer and A1 reflection layer. The invention is characterized by the following: the said record layer and second SiN media layer set with one layer of thermal control film. This invention coats one layer of metal film tightly to record layer as heat transmission layer to control over high temperature of record layer to improve the read valve efficiency and to improve signal to noise proportion.

Description

technical field [0001] The present invention relates to an optical disc for information storage, more specifically to a Blu-ray magneto-optical disc which improves the reading threshold power of the magneto-optical disc under blue light and improves the signal-to-noise ratio. Background technique [0002] With the continuous increase of magneto-optical storage capacity, using short-wavelength laser (blue light) as the recording and reading light source has become an inevitable trend in the development of the next generation of magneto-optical disks. Therefore, the storage medium is required to have a larger Kerr effect at the blue light. Materials such as MnBi, Pt-Co, and garnet oxide have large Kerr angles at short wavelengths, and are candidates for a new generation of magneto-optical storage media. However, there are still many problems to be solved in the practical application of these media. Rare-earth transition metal (TbFeCo) thin films are currently practical magneto...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): G11B11/105G11B7/24G11B5/66G11B7/2433
Inventor 王现英
Owner SHANGHAI INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap