PTFE Membranes and Gaskets Made Therefrom

Abstract

Improved expanded PTFE materials and improved gasket materials made therefrom, the gaskets being capable of forming a seal with greater bolt load retention than is possible with existing PTFE gaskets. The expanded PTFE membranes of the invention can be tailored to exhibit a matrix tensile strength in at least one direction of at least 25,000 psi, a matrix tensile strength ratio in two orthogonal directions of between 0.025 and 4, an orientation index of 50° or less, and a density of 2.0 g / cc or less. The improved gaskets exhibit improved mechanical properties such as high bolt load retention, low creep, high tensile strength, low stress to seal and high crystallinity index.

Description

RELATED APPLICATIONS[0001]The present application is a divisional application of U.S. patent application Ser. No. 11 / 059,849, filed Feb. 16, 2005, which is a divisional application of U.S. patent application Ser. No. 10 / 382,668, filed Mar. 6, 2003 and now abandoned.FIELD OF THE INVENTION[0002]The present invention relates to improved expanded PTFE materials and to improved gaskets made therefrom, the gaskets being capable of forming a seal with greater bolt load retention than is possible with existing PTFE gaskets.BACKGROUND OF THE INVENTION[0003]A wide variety of gaskets are known for use in sealing applications. Expanded polytetrafluoroethylene (PTFE) is widely used today as a gasket material. As disclosed in U.S. Pat. No. 3,953,566 to Gore, this material has numerous properties making it highly desirable as a gasket. These properties include being readily compressible and conformable, being chemically resistant, having relatively high strength, and being far less prone to creep ...

AI Technical Summary

Benefits of technology

[0018]Expanded PTFE membranes of the present invention exhibiting such combinations of improved mechanical properties are prepared by ram extruding a lubricated PTFE powder to form a tape, then calendering, drying, stretching in the machine, or longitudinal, direction at temperatures at or above 325° C., then stretching perpendicular to the machine direction (i.e., the transverse direction) again at temperatures at or above 325° C. while constraining the tape from shrinking in the longitudinal direction, then subjecting the stretched tape to a 380° C. heat zone while constrained. A unique feature of the present invention is that by varying the degree of calendering of the tape, and by varying the stretch temperatures, stretch rates and stretch ratios for both directions, membranes which are surprisingly strong and which have very balanced strengths can be produced. In addition, higher crystallinity and lower orientation indices can be achieved. Suitable processing variations for achieving membranes with these enhanced properties are contained in the Examples herein.

[0019]It was discovered that the improved PTFE membranes of this invention can be incorporated into gasket materials and gaskets exhibiting improved mechanical properties such as high bolt load retention, low creep, high tensile strength, low stress to seal and high crystallinity index. Moreover, it was discovered that PTFE gaskets exhibiting the highest bolt load retention and lowest creep characteristics ever produced could be constructed using these improved PTFE membranes. As used herein for convenience, the term “gasket” is intended to refer to materials in sheet, tape or finished (i.e., cut or shaped, such as annular, etc.) gasket form.

Problems solved by technology

Unfortunately, non-expanded, non-porous PTFE gaskets are generally not conformable enough to effectively seal this type of equipment.

In the case of glass-lined steel flanges, although there is a relatively smooth finish, there is often a large amount of unevenness or lack of flatness associated with the flanges.

Thus, a non-expanded, non-porous PTFE gasket is not conformable enough to seal many of these applications.

Unfortunately, in many of these applications it is not possible to apply sufficient force to the flanges to create enough gasket stress to fully densify the expanded PTFE gasket to create an effective seal.

For example, glass-lined steel piping flanges, glass flanges, or FRP piping flanges may deform, fracture, or break upon the application of a high amount of stress.

Thus, in these applications, an expanded PTFE gasket may not be completely densified to reach a non-porous state, and therefore does not become leak proof, because the maximum stress that can be applied to the flanges without breaking them is not sufficient to so densify the gasket.

While expanded PTFE materials exhibit much better performance than non-expanded, non-porous PTFE in gasket applications, it still exhibits some propensity to creep, or flow, under load.

Typically, the higher the bolt load on a gasket the lower the leakage will be from that gasketed assembly.

PTFE gaskets (i.e., greater than about 50% PTFE, by weight) are prone to creep and stress relaxation when subjected to a compressive load.