Cement based penetrative crystallized waterproof material and its preparation

A technology of waterproof material and osmotic crystallization, applied in cement coatings, antifouling/underwater coatings, paints containing biocides, etc. The effect of good performance, simple construction method and simple construction work

Inactive Publication Date: 2007-11-07
TONGJI UNIV
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the cement-based waterproof materials commonly used at present are surface-sealed waterproofing agents. The waterproof effect only acts on the surface, and cannot automatically and deeply penetrate into the interior of the structure; the waterproof effect is not long-lasting, and a continuous degradation process occurs over time; once If the waterproof coating is damaged, the waterproof ability will be lost; it will easily lead to weak points such as alkali-aggregate reaction (AAR) in concrete

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cement based penetrative crystallized waterproof material and its preparation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0037] High-performance permeable crystalline waterproof material, composed of siloxane, sodium methylnaphthalenesulfonate condensate, potassium aluminum sulfate dodecahydrate, sodium silicate, Portland cement, calcium hydroxide, magnesium hydroxide, bentonite, quartz sand composition. In specific implementation process, each component weight percent is:

[0038]

[0039] According to the above-mentioned ratio and the above-mentioned preparation method, high-performance cement-based permeable crystalline waterproof materials with slightly different performance requirements and suitable for different occasions can be prepared.

[0040] High-performance cement-based permeable crystalline waterproof material, mixed with water at a ratio of 1:0.3-.35 to form a thixotropic, fluid slurry, brushed on the wet concrete base, the active ingredients penetrate into the Inside the concrete, and react to form insoluble crystals such as ettringite. Its active chemical substances undergo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A penetration-crystallization type cement-base water-proof material for building is prepared from silicate cement, sodium methyl naphthalenesulfonate condensate, water silane emulsion, dodecahydrated aluminium potassium sulfate, magnesium hydroxide, calcium hydroxide, sodium silicate, bentone and quartz sand through proportional mixing. Its advantages are high penetrability and crystallinity, permanent water-proof effect, and self-repairing of fine cracking.

Description

technical field [0001] The invention relates to a cement-based waterproof coating material for construction, in particular to a high-performance cement-based waterproof and anti-leakage coating material for cement, mortar, and concrete in water conservancy, hydraulic engineering, hydropower, bridges, tunnels, underground, and construction projects. Penetrates crystalline waterproof coating material. Background technique [0002] Due to its high brittleness, concrete structures often crack inevitably in engineering applications. This kind of cracking leads to the decrease of water tightness and leakage of the concrete structure, which affects the service life of the project, and even cannot be used normally. This is a common problem in the construction industry. There are two main reasons for cracks in concrete structures, one is caused by deformation, including shrinkage, expansion, and uneven subsidence caused by changes in temperature and humidity; the other is caused by...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D1/06C09D5/16
Inventor 蒋正武孙振平
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com