Method for manufacturing carbon nanotube electrocatalytic electrode for organic waste water treatment

A technology of carbon nanotubes and manufacturing methods, which is applied in the field of manufacturing carbon nanotube electrocatalytic electrodes, can solve the problems of poor graphite electrode strength, low electrocatalytic performance, and low current efficiency, and achieve improved electrocatalytic performance and stable chemical properties , Improve the effect of reunion phenomenon

Inactive Publication Date: 2008-07-09
SHANGHAI UNIV
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Graphite electrodes have poor strength and low current efficiency
The aluminum plate or iron plate is a soluble electrode, the material consumption of the electrode itself is large, the cost is high, and the amount of sludge generated is also large
Insoluble electrode PbO 2 Although the oxidation ability of graphite electrode is higher than that of graphite electrode, its electrocatalytic performance is low, and the degradation effect on organic matter is not ideal.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] In this embodiment, the manufacturing method of the carbon nanotube electrocatalytic electrode for treating organic wastewater has the following process steps:

[0020] (1) Purification of carbon nanotube powder: Soak the carbon nanotube powder in 20% nitric acid solution for 24 hours, then ultrasonically disperse it for 2 hours to remove the residual metal catalyst when preparing carbon nanotubes; then carry out suction filtration and wash with distilled water Washed several times until the pH of the eluent was 7, and then dried to constant weight.

[0021] (2) Carry out modification treatment to the purified carbon nanotube powder: the carbon nanotube powder is roasted at a high temperature in an air atmosphere, the roasting temperature is 600° C., and the time is 0.5 hour; 1500rpm.

[0022] (3) Disperse polytetrafluoroethylene (PTFE) binder in carbon nanotubes: use an appropriate amount of polytetrafluoroethylene emulsion, and use absolute ethanol as a solvent, add ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The present invention relates to the making process of carbon nanotube electrically catalytic electrode for treating organic waste water, and belongs to the field of electrode material production in electrically catalytic oxidation technology. After carbon nanotube with high catalytic activity and great specific surface area and binder PTFE in certain ratio are mixed, the mixture is cold pressed to form and wire is led out from one end of the epoxy resin cured electrode. The carbon nanotube electrically catalytic electrode has high conducting performance and low power consumption, and may be modified to obtain high electrically catalytic activity. The carbon nanotube electrically catalytic electrode is suitable for use in treating organic waste water and has high degradation rate on organic matter in waste water.

Description

technical field [0001] The invention relates to a method for manufacturing a carbon nanotube electrocatalytic electrode for treating organic wastewater, and belongs to the technical field of electrode material manufacturing in electrocatalytic oxidation technology. Background technique [0002] The high concentration of organic pollutants, high COD value of chemical oxygen demand and deep water quality in organic wastewater have always been one of the difficult problems in the domestic and foreign scientific and technological circles. After the current treatment technology degrades organic wastewater, the results show that the degradation of organic pollutants is incomplete, the decolorization effect is poor, and the COD removal rate is low, and some treatment technologies are also accompanied by secondary pollution hazards. The electrocatalytic oxidation technology is to make the pollutants undergo direct electrochemical reaction on the electrode or use the strong oxidizing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C25B11/12C02F1/461
Inventor 施利毅温轶方建慧张登松张剑平
Owner SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap