Acrylic resin filmy material, and product with the same

A technology of acrylic resin and film, which is applied in the direction of synthetic resin layered products, layered products, chemical instruments and methods, etc. It can solve the problems of poor forming resistance to whitening, poor light return resistance, and unsuitable laminated films or flakes, etc., to achieve the effect of excellent scratch resistance and whitening resistance

Active Publication Date: 2007-08-29
MITSUBISHI CHEM CORP
View PDF30 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the acrylic resin films described in References 26 to 28 do not describe their light back resistance, and the acrylic resin films using the resin composition described in the examples as raw materials do not have any expected light back resistance. A level for building materials, not suitable for laminated films or sheets for building materials
[0050] On the other hand, when an acrylic resin film with excellent heat resistance (for example, references 1 to 4) is used, it is excellent in light reflection resistance, but it is not suitable for use as a laminate for building materials because of poor molding whitening resistance. film or sheet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acrylic resin filmy material, and product with the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0780] To 100 parts of the multilayer structure polymer (I-1), 2.7 parts of the product name "Chiubin 234" manufactured by Chiba Special Chemical Co., Ltd., and 0.1 parts of the product name "Adecastab AO-50" manufactured by Asahi Denka Co., Ltd. part, and 0.3 part of the product name "Adecastab LA-57" manufactured by Asahi Denka Kogyo Co., Ltd., and mixed with a Henschel mixer. This mixture [resin composition (III-1)] was heated to 230°C, supplied to a degassing extruder (PCM-30 (trade name) manufactured by Ikegai Iron Works Co., Ltd.), and kneaded to obtain pellets. .

[0781] Dry the granules produced by the above method at 80°C for a whole day and night, and use a 40mm φ non-bending screw extruder (L / D=26) with a 300mm wide T-die installed, at a barrel temperature of 180-240°C, T-die A film was formed at a temperature of 240° C. to obtain a 125 μm thick acrylic resin film (A). Formation of the decorative layer (B) was good, and there were few printing omissions.

Embodiment 2

[0783] In addition to using 90 parts of multilayer structure polymer (I-1) and thermoplastic polymer (II-1) [MMA / MA=99 / 1 (mass ratio), reduced viscosity ηsp / c=0.06L / g] instead of 10 parts Except for 100 parts of the multilayer structure polymer (I-1), a mixture [resin composition (III-2)] was obtained in the same manner as in Example 1, and a film was formed to obtain an acrylic resin film (A). Formation of the decorative layer (B) was good, and there were few printing omissions.

Embodiment 3

[0785] Except using 75 parts of multilayer construction polymers (I-1) and 25 parts of thermoplastic polymers (II-1) to replace 100 parts of multilayer construction polymers (I-1), the mixture [resin Composition (III-3)] was formed into a film to obtain an acrylic resin film (A). Formation of the decorative layer (B) was good, and there were few printing omissions.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
heat deflection temperatureaaaaaaaaaa
flexural modulusaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to view more

Abstract

An acrylic resin film material comprising at least a multilayer structure polymer with a particular structure prevent a molded item from being whitened during insert- or in-mold molding and meet the requirement for surface hardness, heat resistance, and transparency or matting performance for vehicle applications. It is also possible to use an acrylic resin film material exhibiting a difference of 30% or less between haze values as determined in accordance with the testing method of JIS K7136 (haze measurement method) after and before a tensile test where a test piece with a width of 20 mm is pulled under the conditions of an initial inter-chuck distance of 25 mm, a rate of 50 mm / min and a temperature of 23 DEG C. until an end-point inter-chuck distance becomes 33 mm as well as having a pencil hardness of 2 B or higher as determined in accordance with JIS K5400.

Description

[0001] The application date of the original application is December 26, 2003, the application number is 200380108060.5, and the title of the invention is "multilayer structure polymer and resin composition, and acrylic resin film, acrylic resin laminated film, photocuring A divisional application of a Chinese patent application for permanent acrylic resin films and sheets, laminated films and sheets, and laminated products laminated with these. technical field [0002] The present invention relates to multilayer structure polymers and resin compositions, acrylic resin films, acrylic resin laminated films, photocurable acrylic resin films and sheets, laminated films and sheets, and laminated moldings in which these are laminated Taste. Background technique [0003] As a method of imparting a pattern to a molded product at low cost, there are insert molding or inmold molding. The insert molding method is to form a film or sheet of polyester resin, polycarbonate resin, acrylic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08J5/18B32B27/30B29C45/14C08L33/00
Inventor 北池幸雄安部善纪阿部纯一北岛浩一郎冈崎正吾藤井秀幸
Owner MITSUBISHI CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap