Non-stick coating and preparation method thereof, pot, and cooking equipment

A technology of non-stick coatings and pots, which is applied in coatings, metal material coating processes, kitchen utensils, etc., and can solve problems such as coating life and application limitations, coating peeling, failure, and low coating adhesion , to achieve high bonding strength, good wear resistance, and good non-stick effect

Active Publication Date: 2018-12-11
FOSHAN SHUNDE MIDEA ELECTRICAL HEATING APPLIANCES MFG CO LTD
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing non-stick coatings are mainly Teflon PTFE non-stick coatings or ceramic non-stick coatings. These coatings are usually formed by air pressure spraying, electrostatic spraying, and then high temperature sintering and curing. , and the service life of this kind of coating is generally only half a year to one year, and the coating hardness is low (the Vickers hardness of PTFE non-stick coating is 100-200HV, the Vickers hardness of ceramic non-stick coating is 200-350HV), The coating adhesion is small (the bonding force of PTFE non-stick coating is 2-10MPa, the bonding force of ceramic non-stick coating is 2-5MPa), the coating thickness is small (the thickness of PTFE non-stick coating is 20-50μm , the thickness of the ceramic non-stick coating is 20-40μm), the acid and alkali resistance and salt resistance are also average. During long-term use, scratches, wear and corrosion will inevitably cause the coating to fall off and fail. When the surface is coated with After the layer fails, this non-stick coating will not be non-stick, which limits the life and application of the coating to a large extent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-stick coating and preparation method thereof, pot, and cooking equipment
  • Non-stick coating and preparation method thereof, pot, and cooking equipment
  • Non-stick coating and preparation method thereof, pot, and cooking equipment

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0067] (1) 47.6kg of common PFA powder, 0.4kg of polyvinyl alcohol, 2kg of glycerin and 50kg of water are mixed to prepare a slurry;

[0068] (2) The slurry is subjected to airflow atomization drying treatment, wherein the conditions of airflow atomization drying include: the atomization pressure is 0.4MPa, and the atomization air flow rate is 2m 3 / h, the inlet temperature is 320°C, and the outlet temperature is 100°C to obtain modified PFA powder S1.

[0069] It is determined that the particle size D50 of the modified PFA powder is 52 μm, the sphericity of 96% of the powder is 95%, the fluidity is 15s / 50g, and the purity is 99.9%. The microscopic morphology of the modified PFA powder is shown in figure 1 shown.

preparation example 2

[0071] (1) 54.8kg common PFA powder, 0.2kg polyvinyl chloride, 3kg paraffin and 42kg water are mixed to prepare slurry;

[0072] (2) The slurry is subjected to airflow atomization drying treatment, wherein the conditions of airflow atomization drying include: the atomization pressure is 0.3MPa, and the atomization air flow rate is 1m 3 / h, the inlet temperature is 300°C, and the outlet temperature is 60°C to obtain modified PFA powder S2.

[0073] It is determined that the particle size D50 of the modified PFA powder is 46 μm, the sphericity of 95% of the powder is 93%, the fluidity is 13s / 50g, and the purity is 99.5%.

preparation example 3

[0075] (1) 38.5kg common PFA powder, 0.5kg polyacrylate, 1kg graphite and 60kg water are mixed to prepare slurry;

[0076] (2) The slurry is subjected to airflow atomization drying treatment, wherein the conditions of airflow atomization drying include: the atomization pressure is 0.5MPa, and the atomization air flow rate is 3m 3 / h, the inlet temperature is 350°C, and the air outlet temperature is 140°C to obtain modified PFA powder S3.

[0077] It is determined that the particle size D50 of the modified PFA powder is 59 μm, the sphericity of 95% of the powder is 98%, the fluidity is 18s / 50g, and the purity is 99.9%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Fluidityaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of electric heating appliances, and discloses a non-stick coating and a preparation method thereof, a pot, and cooking equipment. The method comprises: (1)pre-treating a matrix; (2) pre-heating the surface of the matrix obtained in the step (1); and (3) mixing silicon carbide powder and fluororesin powder to obtain a powder mixture, and carrying out plasma spraying treatment with the powder mixture to form a non-stick coating on the surface of the matrix. The non-stick coating of the invention is gray-black, and has advantages of scale resistance,high surface hardness, high coating adhesion, good scratch resistance, good corrosion resistance, good wettability, good heat transfer performance, long service life and the like.

Description

technical field [0001] The invention relates to the technical field of electric heating appliances, in particular to a non-stick coating, a preparation method thereof, pots and cooking equipment. Background technique [0002] The existing non-stick coatings are mainly Teflon PTFE non-stick coatings or ceramic non-stick coatings. These coatings are usually formed by air pressure spraying, electrostatic spraying, and then high temperature sintering and curing. , and the service life of this kind of coating is generally only half a year to one year, and the coating hardness is low (the Vickers hardness of PTFE non-stick coating is 100-200HV, the Vickers hardness of ceramic non-stick coating is 200-350HV), The coating adhesion is small (the bonding force of PTFE non-stick coating is 2-10MPa, the bonding force of ceramic non-stick coating is 2-5MPa), the coating thickness is small (the thickness of PTFE non-stick coating is 20-50μm , the thickness of the ceramic non-stick coatin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C4/134C23C4/04A47J27/00A47J27/086A47J36/02A47J37/08
CPCA47J27/00A47J27/086A47J36/025A47J37/08C23C4/04
Inventor 李兴航曹达华黄宇华杨玲李康屈雪平李洪伟
Owner FOSHAN SHUNDE MIDEA ELECTRICAL HEATING APPLIANCES MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com