Process for making a thermoplastic vulcanizate composition

A thermoplastic vulcanization and thermoplastic technology, which can solve problems such as difficulty in adding water, and achieve the effect of flexible selection

Inactive Publication Date: 2008-05-28
MOMENTIVE PERFORMANCE MATERIALS INC
View PDF9 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, adding water to the extruder at temperatures well above its boiling point is a difficult process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0049] The following materials were used in the examples and comparative examples:

[0050] Royalene(R) 694 EPDM rubber: terpolymer of ethylene, propylene, and non-conjugated diene, filled with 75 phr of clear, non-staining paraffin oil. Obtained from Uniroyal Chemical.

[0051] Royalene(R) 4697 EPDM rubber: terpolymer of ethylene, propylene, and non-conjugated diene, filled with 100 phr white hydrotreated paraffin oil. Obtained from Uniroyal Chemical.

[0052] Profax TM 6523: Commonly used propylene homopolymer. Obtained from Basell Service Co.

[0053] Engelhard(R) clay: a calcined and surface treated aluminosilicate available from Engelhard Co. under the name Translink(R).

[0054] Burgess(R) Clay: Untreated aluminosilicate.

[0055] Naugard(R) 10: Antioxidant for rubber.

[0056] Silcross(R) 11: A blend of Silquest(R) A-1100 aminosilane and white oil, available from the General Electric Company.

[0057] A single screw rotary and reciprocating kneader from BUSS wa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A process for making a thermoplastic vulcanizate includes blending a thermoplastic first polymer, an elastomeric second polymer, a carboxylic anhydride, a free radical generator, and a particulate reinforcing material to provide a first blend containing the thermoplastic first polymer and grafted elastomeric second polymer with the particulate reinforcing material dispersed therein, the particulate reinforcing material having sufficient surface moisture to permit coupling to the thermoplastic first polymer and the elastomeric second polymer upon reaction with a coupling agent; then, combining a coupling agent with the first blend for coupling the thermoplastic first polymer and / or grafted elastomeric second polymer with the particulate reinforcing material and / or crosslinking the grafted elastomeric second polymer.

Description

Background of the invention [0001] Thermoplastic elastomers (TPEs) have the functional properties of conventional thermoset rubbers, and they are also capable of being melted repeatedly, making them suitable for processing in conventional thermoplastic manufacturing equipment. Most TPEs consist of two phases, one phase consisting of a rubber material (elastomer) that is insoluble in the other phase, and the other phase being a flowable thermoplastic material. The rubber material exists as a dispersed phase and the thermoplastic material as a continuous phase. [0002] Although in principle it is not necessary to cross-link the rubber within a TPE, the use of cross-linking technology has proven effective in obtaining better chemical resistance, mechanical properties and better phase separation control. Such TPE compositions in which crosslinking reactions and processes are used to separate the phases into separate domains are known as thermoplastic vulcanizates (TPVs). In ord...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L51/06C08L23/10
CPCC08L23/08C08L23/16C08K5/14C08L23/04C08L51/06C08L21/00C08K5/54C08L23/10C08L2666/06C08L2666/24C08J3/24C08L51/00C08K3/26C08L23/00
Inventor 路易斯·M·潘泽尔菲尔贝·E·拉姆达特
Owner MOMENTIVE PERFORMANCE MATERIALS INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com