Fine denier light terylene short fine with luminous function
A bright polyester, functional technology, applied in the field of polyester staple fiber, can solve the problem of no polyester bright staple fiber, etc., and achieve the effect of uniform shrinkage, good dimensional stability, and good gloss
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0011] The following is a specific embodiment of the present invention:
[0012] The production process is as follows: the intrinsic viscosity IV of the super-gloss polyester chips is 0.64dl / g, and the fluorescent agent is added to the chips at the mixing silo at a ratio of 0.15%, and then sent to the wet chip silo through pulse conveying, and then enters after drying. In the screw extruder, the set temperature of the extruder is 270~285℃, the melt pressure is more than 10MPa, and the melt temperature is 290℃. It is measured by a variable frequency metering pump. After the pump, the melt pressure is 15MPa, and it is mixed by a high-efficiency static mixer. , Enter the spinning box for spinning, the melt is passed through the circular spinneret, the resulting tow is cooled by ring blowing, oiled and wound down the barrel to obtain the nascent fiber, and then bundled, drawn, crimped, relaxed and heat-set , Cut and pack to produce the polyester staple fiber described in this embodime...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap