Solvent-free non-toxic coating for large-scale container internal wall
A non-toxic coating and large-scale container technology, applied in the field of coating manufacturing, can solve the problems of unusable inner walls of containers and pipes, expensive PTFE coatings, etc., and achieve the effect of energy saving
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0038] The preparation of embodiment 1 modified epoxy resin
[0039] Raw material parts by weight
[0040] Epoxy resin E51 54
[0041] Polysulfide rubber PS1000 40
[0042] n-Butyl glycidyl ether 6
[0043] Feed into the reaction kettle according to the above ratio, raise the temperature to 90°C, and add 0.03 part of catalyst 2,4,6-tris(dimethylaminomethyl)phenol while stirring. React for 3 hours while stirring under heat preservation at 90° C. to obtain a yellowish brown transparent liquid polysulfide rubber modified epoxy resin.
Embodiment 2
[0044] Embodiment 2 Preparation of solvent-free and non-toxic paint
[0045] Take by weighing 80 parts by weight of E51 epoxy resin, adopt 20 parts by weight of modified epoxy resin of embodiment 1, drop into the stainless steel tank and stir with a high-speed mixer, add defoamer BYK-055 and DEH6800 altogether 1.02 parts by weight, wetting 0.45 parts by weight of dispersant BYK-P104S, 0.03 parts by weight of leveling agent BYK-322, stir evenly with resin, add 1.3 parts by weight of titanium dioxide, 14.5 parts by weight of precipitated barium sulfate, thixotropic agent (organic bentonite) B-27 # 1.4 parts by weight are further stirred evenly, and then ground to a standard fineness with a sand mill or a three-roll mill, filtered and loaded into a barrel to become component A of the coating.
[0046] Use commercially available modified aromatic amine curing agent K4170 parts by weight, defoamer BYK-055 and DEH6800 total 1.0 parts by weight, wetting and dispersing agent (BYK-P104...
Embodiment 3
[0055]Embodiment 3 The preparation of modified epoxy resin and the preparation of coating
[0056] Raw material parts by weight
[0057] Epoxy resin R140 50
[0058] Polysulfide rubber PS1000 42
[0059] n-Butyl glycidyl ether 8
[0060] The preparation process is the same as in Example 1, and a yellow-brown transparent liquid polysulfide rubber-modified epoxy resin is obtained.
[0061] When preparing the paint, 65 parts by weight of epoxy resin DER331 was used together with 35 parts by weight of the modified epoxy resin prepared in Example 3, and the rest were the same as in Example 2. Coatings with similar properties and effects are obtained.
PUM
Property | Measurement | Unit |
---|---|---|
adhesivity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap