Waterproof coating material

A waterproof coating and coating technology, applied in antifouling/underwater coatings, coatings, paints containing biocides, etc., can solve the rising cost of waterproof coatings and anti-corrosion coatings, the reduction of coating protection ability, and the damage of anti-corrosion or waterproof layer. and other problems to achieve the effect of prolonging curing time, increasing density and strength, and resisting acid corrosion.

Inactive Publication Date: 2010-07-28
王丹
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The problem is that the outermost coating, whether it is a waterproof layer or an anti-corrosion layer, will be damaged under the action of acid rain, and the built-in anti-corrosion or waterproof layer will also be damaged, reducing the coating's ability to protect the building body
[0003] In addition, some of the existing waterproof coatings are harmful to the human body and the environment, such as solvent-based waterproof coatings and polyurethane waterproof coatings.
Many of the existing waterproof coatings and anti-corrosion coatings are prepared using petroleum as raw materials. In the case of increasingly tight oil resources, the cost of waterproof coatings and anti-corrosion coatings will inevitably increase.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A. React natural crystalline sulfur with a modifier to generate a sulfur polymer with a network polymer structure. The specific method is to heat the sulfur to 120°C and mix it with the modifier. The weight of the modifier is 2%. , and continue to heat the sulfur-generating polymer. The modified sulfur polymer has strong stability, strong waterproof, anti-seepage and corrosion resistance, and good quick-drying property.

[0027] Modifiers can be aromatic hydrocarbons, such as styrene, vinyltoluene, methylstyrene, etc.; they can also be diene (genus) hydrocarbons or olefinic hydrocarbons, such as: 2,3 - indane, dicyclopentadiene. The modifier may be one or a combination of two or more of the above compounds.

[0028] B, after the polymer melting of the sulfur that step A obtains is sprayed to form waterproof, anti-corrosion layer through cleaning and drying in advance on the surface layer, the thickness of waterproof, anti-corrosion layer should be 0.3mm-1MM to play wa...

Embodiment 2

[0030] A. The difference from step A in Example 1 is that the sulfur is refined from petroleum or desulfurized from natural gas, and the weight of the modifier is 10%. The modification process needs to mix the natural sulfur with the modifier after being heated to 150° C. Continued heating yields polymers of sulfur.

[0031] B, then mix solid powder in the polymer that obtains sulfur, preferably fly ash, its particle is uniform, with low cost, main purpose is to increase the strength and density of the material of the present invention, improve water resistance and impermeability. Solid powder can also choose one or a mixture of several of the following materials: fly ash after coal combustion, steel slag, ash after garbage incineration, construction waste ash, solid waste powder from chemical plants , Radioactive solid waste particles. The mixing amount of the solid powder should be 3%-10% (weight ratio) of the sulfur polymer, and the inorganic solid powder should be 50 mesh...

Embodiment 3

[0034] With step A difference in the embodiment 2, the weight of modifier is 25%, and the heating melting temperature of sulfur is 160 DEG C; Mix with the polymer weight 10%-20% (weight ratio) of sulfur with solid powder weight, solid The powder is preferably steel slag, and its particle size is 80 mesh. It is sprayed on the surface layer after hot stirring and mixing, and its purpose is to improve the wear resistance of the surface layer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pressureaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

To solve the problem that the prior art has no paint with waterproof, watertight and anticorrosive performances, the invention provides waterproof paint with good waterproof, watertight and anticorrosive performances. The waterproof paint comprises a sulfur polymer which has a netted macromolecule structure and also comprises solid powder particles interfused into the polymer. The waterproof paint can be applicable for a waterproof, watertight and anticorrosive pool of concrete, tunnels, underground, bridge surfaces and chemical plants, a methane pool and other surfaces which need waterproofing and anticorrosion.

Description

technical field [0001] The invention belongs to a waterproof coating, in particular to a waterproof coating for the construction field. Background technique [0002] The coatings used in construction are mainly divided into waterproof coatings and anti-corrosion coatings, which have the functions of waterproof, anti-seepage and anti-corrosion respectively. In practical applications, the coating layer is often required to have waterproof and anti-corrosion functions at the same time. For example, the impact of acid rain is increasing, and external coatings are required to be waterproof and acid-resistant at the same time. Utilize existing technology to only be coated with waterproof coating and anticorrosion coating respectively to form waterproof layer and anticorrosion layer. The problem is that the outermost coating, whether it is a waterproof layer or an anti-corrosion layer, will be damaged under the action of acid rain, and the built-in anti-corrosion or waterproof lay...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D201/02C09D5/16C09D7/12
Inventor 王丹
Owner 王丹
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com