Method for preparing high performance flame-retardant terylene inner decoration textile fabric

A flame-retardant polyester and textile technology, which is applied in the field of preparation of high-performance flame-retardant polyester interior textiles, can solve the problems of fabric discoloration, poor durability of flame-retardant effect, serious fabric droplets, etc.

Inactive Publication Date: 2009-05-06
DONGHUA UNIV +1
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

This patented technology allows for testing both qualitative and quantitatively how well it prevents fire hazards caused by flames or gases from burning fabrics made with materials like Polyethylene Terephthalate (PET). It also compares different types of fibers used together without causing any harmful side reactions that could affect their properties.

Problems solved by technology

This patents discusses how important factors affect the flamproofness/combibility of polyesters during their use in garment applications such as clothing, upholstery products, furniture cushions, automobile seat covers, etc., due to their ability to resist flames while maintaining flexibility at room temperatures. However, these technical effects make polyester surfaces vulnerable towards flaming attacks, especially those involving small particles called fine powders. Additionally, they often come off easily because of friction between themselves and objects placed nearby, causing harmful impacts like scaldings. Therefore, improving the flarnhold property of polyurethane composites requires developing better flame protection than existing ones.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing high performance flame-retardant terylene inner decoration textile fabric
  • Method for preparing high performance flame-retardant terylene inner decoration textile fabric
  • Method for preparing high performance flame-retardant terylene inner decoration textile fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The manufacturing method of high-performance flame-retardant polyester interior textiles is as follows: prepare coating slurry [its components and volume content include: the amount of water-based polyurethane dispersion is 60%, flame retardant (main structure is ) dosage is 30%, SiO 2 Synergist 2.5%, the amount of thickener KF is 7.5%] → coated polyester fabric (gluing amount is 160g / m 2 ) → bake at 150°C for 2 minutes. The flame retardant properties of polyester interior textiles treated by this process are shown in Table 1-3.

[0020] Table 1 Combustion performance

[0021]

[0022] Table 2 Test data of smoke density experiment

[0023]

[0024] Table 3 Test data of smoke toxicity experiment

[0025]

Embodiment 2

[0027] The manufacturing method of high-performance flame-retardant polyester interior textiles is: preparing coating slurry [its components and volume content include: the amount of water-based polyurethane dispersion is 65%, flame retardant (main structure is ) dosage is 28%, SiO 2 Synergist 2%, the amount of thickener KF is 5%] → coated polyester fabric (gluing amount is 180g / m 2 ) → bake at 150°C for 2 minutes. The flame retardant properties of polyester interior textiles treated by this process are shown in Table 4-6.

[0028] Table 4 Combustion performance

[0029]

[0030] Table 5 Test data of smoke density experiment

[0031]

[0032] Table 6 Test data of smoke toxicity experiment

[0033]

Embodiment 3

[0035] The manufacturing method of high-performance flame-retardant polyester interior textiles is as follows: prepare coating slurry [its components and volume content include: the amount of water-based polyurethane dispersion is 55%, flame retardant (main structure is ) dosage is 35%, SiO 2 Synergist 2%, the amount of thickener KF is 8%] → coated polyester fabric (gluing amount is 200g / m 2 ) → bake at 150°C for 2 minutes. The flame retardant properties of polyester interior textiles treated by this process are shown in Table 7-9.

[0036] Table 7 Combustion performance

[0037]

[0038] Table 8 Test data of smoke density experiment

[0039]

[0040] Table 9 Test data of smoke toxicity experiment

[0041]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing a high-performance flame-retardant terylene interior textile, which comprises the following steps: (1) coating slurry is prepared, and comprises the following compositions with the volume content: 50 to 70 percent of waterborne polyurethane dispersion liquid, 25 to 40 percent of a flame retardant, 2 to 3 percent of SiO2 synergistic agent, and 3 to 8 percent of thickening agent; and (2) a terylene fabric is coated, the sizing amount is between 160 and 240g/m<2>, and the baking is performed for 2 to 5min at a temperature of between 150 and 180 DEG C. The combustion performance of the textile obtained by the method reaches the national level B1, and the terylene fabric basically has no fused drops; smoke density and smoke toxicity tests reach grade F3 in French NF F16-101-1998 standard; and the smoke density tests meet the requirement of Boeing BSS7238 standard, and the smoke toxicity tests meet the requirement of Boeing BSS7239 standard.

Description

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap