Wax shale gray slag base polymer gelled material

A technology of oil shale ash and polymer glue, which is applied in the field of light building materials, can solve problems such as adverse effects on the surrounding environment, environmental pollution, waste of resources, etc., and achieve low production prices, huge economic and social benefits, and a wide range of applications Effect

Inactive Publication Date: 2009-07-29
FUSHUN MINING IND GROUP
View PDF0 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Oil shale ash is the product of oil shale dry distillation, which belongs to slag waste, and a large amount of accumulation causes serious environmental pollution and waste of resources
At present, the treatment methods of oil shale ash are mainly landfill and accumulation. Since there is no mature comprehensive utilization method, it not only causes a relatively large adverse impact on the surrounding environment, but also is a huge waste of resources.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wax shale gray slag base polymer gelled material
  • Wax shale gray slag base polymer gelled material
  • Wax shale gray slag base polymer gelled material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Blend 37% oil shale ash with 31% calcined kaolin, 17% cement, 5% quicklime, and 4% industrial alkali. After mixing evenly, add 8% activator, and add 5 to 25 %, mixed and stirred for 2 minutes to obtain a composite slurry. The composite molding material is gray after solidification, can be colored, has a hard texture and good plasticity.

Embodiment 2

[0030] Blend 47% oil shale ash with 21% calcined kaolin, 15% cement, 4% quicklime, and 3% industrial alkali. After mixing evenly, add 8% activator, and add 5 to 25 %, mixed and stirred for 2 minutes to obtain a composite slurry. The composite molding material is gray after solidification, can be colored, has a hard texture and good plasticity.

Embodiment 3

[0032] Blend the oil shale ash with a weight ratio of 58% with 10% calcined kaolin, 17% cement, 4% quicklime, and 4% industrial alkali. %, mixed and stirred for 2 minutes to obtain a composite slurry. The composite modeling material is dark gray after solidification, can be colored, has a hard texture and good plasticity.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a cementing material of an oil shale clinker matrix polymer and a preparation method thereof, and belongs to the field of environment-friendly materials. The cementing material comprises the following components in percentage by weight: 30 to 70 percent of oil shale clinker with the particle diameter of 200 meshes, 0 to 70 percent of low-temperature calcined kaolin with particle diameter of 200 meshes, 0 to 10 percent of calcium lime with the fineness of 150 meshes, 5 to 30 percent of P32.5 cement, and 5 to 10 percent of exciting agent, wherein the exciting agent is a mixed solution of industrial sodium silicate of which modulus M is 3.3 and industrial alkali. The cementing material can replace the prior cementing material gypsum and cement, and is suitable for manufacturing stone imitated artworks, embossing wall bricks, sculptures and ground tiles for building decoration and products such as hollow bricks, light bricks, and the like for building materials. The cementing material has low cost and performance superior to the prior material.

Description

[0001] The invention relates to a geopolymer cementitious material whose main component is oil shale ash and a preparation method thereof. The cementitious material uses the oil shale ash, which is the waste produced in the dry distillation process of Fushun Mining Group, as the main raw material, uses low-temperature calcined kaolin and cement as reinforcing materials, and adds quicklime and an appropriate amount of activator materials, such as sodium hydroxide Or potassium hydroxide, which is obtained by blending and stirring with a mixer for a certain period of time. technical field [0002] The invention relates to a method for preparing a gelled material, which belongs to the technology of light building materials, and specifically relates to a method for preparing and using a mineral waste slag-based geopolymer material. Background technique [0003] Oil shale ash is the product of oil shale dry distillation, which belongs to slag waste, and a large amount of accumulat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B7/30C04B7/36
CPCC04B20/04C04B28/026
Inventor 韩放刘剑虹鲍明福高健李理袁平恩鞠广生贾宝栋
Owner FUSHUN MINING IND GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products