Method for preparing active carbon

A technology for preparing activated carbon and raw materials, which is applied in the field of preparation of adsorption materials, can solve problems such as micropore blockage and carbon structure damage, and achieve the effects of increasing specific surface area, cleaning the process, and alleviating energy shortage

Inactive Publication Date: 2009-08-05
CENT SOUTH UNIV
View PDF0 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to solve the problem of organic gas damage to carbon structure and micropore blockage when preparing activated carbon by traditional zinc chloride activation method, and to provide a method for preparing acti

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing active carbon
  • Method for preparing active carbon
  • Method for preparing active carbon

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] When the mass ratio of the raw material Chinese fir sawdust to zinc chloride is 1:1, the Chinese fir sawdust is immersed in the zinc chloride solution for 24 hours, and the dried sample is weighed and placed in the reaction furnace, and vacuumized. The activated carbon is prepared under the conditions of system pressure of 10.5kPa, heating rate of 5°C / min, final cracking temperature of 400°C, and holding time of 60min. After testing, the iodine adsorption value of the prepared activated carbon was 916.28 mg / g, and the methylene blue adsorption value was 250.14 mg / g.

Embodiment 2

[0021] When the mass ratio of the raw material Chinese fir sawdust to zinc chloride is 1:1, the Chinese fir sawdust is immersed in the zinc chloride solution for 24 hours, and the dried sample is weighed and placed in the reaction furnace, and vacuumized. The activated carbon was prepared under the condition that the system pressure was 50.5kPa, the heating rate was 5°C / min, the cracking final temperature was 500°C, and the holding time was 60min. After testing, the prepared iodine adsorption value is 976.68 mg / g, and the methylene blue adsorption value is 323.28 mg / g.

Embodiment 3

[0023] When the mass ratio of the raw material Chinese fir sawdust to zinc chloride is 1:1, the Chinese fir sawdust is immersed in the zinc chloride solution for 24 hours, and the dried sample is weighed and placed in the reaction furnace, and vacuumized. Under the condition that the system pressure is 30.5kPa, the heating rate is 5°C / min, the final cracking temperature is 500°C, and the holding time is 60min, the SEM photo of the activated carbon is shown in the attached figure 2 . After testing, the prepared iodine adsorption value is 1008.69 mg / g, and the methylene blue adsorption value is 321.61 mg / g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Adsorption valueaaaaaaaaaa
Adsorption value of methylene blueaaaaaaaaaa
Iodine adsorption valueaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for preparing active carbon, which comprises the following steps: crushing, sieving and drying woody raw materials, soaking the raw materials into a zinc chloride solution according to the mass ratio of the raw materials to zinc chloride of 1:1-4, and drying the solution; performing cracking activation under the vacuum condition, wherein the temperature rise rate is between 5 and 15 DEG C per minute, and the cracking final temperature is between 400 and 500 DEG C; maintaining at the cracking final temperature for approximately 1 hour; and performing acid washing, water washing and drying on the reaction product to obtain the product, namely the active carbon. Compared with active carbon prepared under the condition of normal pressure, the active carbon prepared by the method has the advantages that the micropore rate is improved by 5.34 to 13.18 percent, the specific surface area is increased by 6.21 to 20.31 percent, and the adsorption performance is superior. Moreover, a byproduct, namely biological oil, can be collected when the active carbon is obtained simultaneously, so that the resource utilization rate is high and the energy consumption is reduced.

Description

technical field [0001] The present invention relates to the preparation of adsorption materials, in particular to the preparation of activated carbon. Background technique [0002] Activated carbon has a rich pore structure and a huge specific surface area. The surface of the carbon contains a variety of oxygen-containing functional groups. It has good catalytic activity and chemical stability, high mechanical strength, and is easy to use repeatedly. This series of excellent characteristics makes it a kind of preparation A high-quality adsorbent that has attracted worldwide attention. [0003] Activated carbon can be made from various carbonaceous substances. In today's increasingly serious energy crisis and environmental problems, it is of great strategic significance to develop and utilize clean agricultural and forestry wastes and other biomass resources. For my country, a country with a large population, large agriculture, and large energy consumption, using biomass re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01B31/08C01B31/12
Inventor 丘克强杨娟
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap