Artificial stone with health function and preparation method thereof

An artificial stone and functional technology, applied in the field of artificial stone, can solve the problem of electromagnetic wave hazard and other problems, and achieve the effect of good shielding and absorption, and large specific surface area.

Active Publication Date: 2009-11-18
延吉可喜安医疗器械有限公司
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The medical stone medicine stone provided by the above patent cannot solve the problem of harm caused by electromagnetic waves to the human body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] (1) Weigh 20 kg of medical stone powder with a particle size of 25 μm to 48 μm; weigh a particle size of 24 μm to 45 μm and a specific surface area of ​​750 m 2 35kg of bamboo charcoal powder per gram; Weigh 15kg of tourmaline with particle size of 26μm~43μm; Weigh 6kg of biotite powder with particle size of 24μm~48μm; Weigh 10kg of albite powder with particle size of 28μm~47μm; Weigh with particle size of 22μm ~43μm clay 18kg;

[0038] (2) After mixing the above raw material powder with 9.4kg water, stir evenly;

[0039] (3) The stirred mixture is made into particles with a particle size of 200 μm to 300 μm in a spheroidizer;

[0040] (4) drying the particles at 200° C. for 2 hours;

[0041] (5) Compressing the dried particles into a plurality of sheets with a thickness of 5mm under the condition of 1000MPa;

[0042] (6) Sinter the flakes obtained by pressing and forming in a nitrogen atmosphere in a muffle furnace under normal pressure, the sintering temperature is...

Embodiment 2

[0080](1) Weigh 35 kg of medical stone powder with a particle size of 25 μm to 48 μm; weigh a particle size of 24 μm to 45 μm and a specific surface area of ​​750 m 2 / g bamboo charcoal powder 20kg; Weigh 25kg of tourmaline with a particle size of 26μm-43μm; Weigh 10kg of biotite powder with a particle size of 24μm-48μm; Weigh 7kg of albite powder with a particle size of 28μm-47μm; Weigh a particle size of 22μm ~43μm clay 28kg;

[0081] (2) After mixing the above-mentioned raw material powder with 10kg of water, stir evenly;

[0082] (3) The stirred mixture is made into particles with a particle size of 300 μm to 400 μm in a spheroidizer;

[0083] (4) drying the particles at 220° C. for 2 hours;

[0084] (5) Compressing the dried particles into a plurality of sheets with a thickness of 5mm under the condition of 1500MPa;

[0085] (6) Sinter the flakes obtained by pressing and molding under normal pressure in a nitrogen atmosphere in a muffle furnace. The sintering temperatu...

Embodiment 3

[0123] (1) Weigh 30 kg of medical stone powder with a particle size of 25 μm to 48 μm; weigh a particle size of 24 μm to 45 μm and a specific surface area of ​​750 m 2 32kg of bamboo charcoal powder per gram; Weigh 20kg of tourmaline with a particle size of 26μm-43μm; Weigh 8kg of biotite powder with a particle size of 24μm-48μm; Weigh 9kg of albite powder with a particle size of 28μm-47μm; Weigh a particle size of 22μm ~43μm clay 20kg;

[0124] (2) After mixing the above-mentioned raw material powder with 11kg of water, stir evenly;

[0125] (3) Granulating the stirred mixture in a spheroidizer to form particles with a particle size of 300 μm to 400 μm;

[0126] (4) drying the particles at 230° C. for 2 hours;

[0127] (5) Compressing the dried particles into several sheets with a thickness of 5mm under the condition of 1500MPa;

[0128] (6) Sinter the flakes obtained by compression molding under normal pressure in a nitrogen atmosphere in a muffle furnace, the sintering t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides an artificial stone with health function, comprising the following components by weight proportion: 20 to 35 portions of medical stone, 20 to 35 portions of bamboo charcoal, 15 to 25 portions of tourmaline, 6 to 10 portions of biotite, 7 to 10 portions of feldspar and 18 to 28 portions of clay. Compared with the prior art, the artificial stone releases far infrared ray and negative ions with health function to human body, and also simultaneously has good screening and absorptive action to harmful electromagnetic wave with the frequency of 10Hz to 1000MHz. In addition, the artificial stone, relatively to other materials, has large specific surface area of bamboo charcoal, absorbs more volatilizable liquid, and is more beneficial to making a plurality of materials into formed bodies with higher strength under the capillary action of volatilizable liquid, thus making the artificial stone with higher strength.

Description

technical field [0001] The invention relates to an artificial stone, in particular to an artificial stone with health care function and a preparation method thereof. Background technique [0002] Negative ions and far infrared rays have important health care functions for human health. Among them, negative ions are a kind of negatively charged gas ions in the air, which have the effect of purifying the air. Because negative ions have various effects on the human body such as sedation, hypnosis, analgesia, suppression, cough relief, antipruritic, diuretic, appetite increasing, and blood pressure lowering, it is also called "air vitamin" or "longevity element". The places where a large amount of negative ions are produced are forests, seashores, and waterfalls. In these environments, the concentration of negative ions is high, so people will feel refreshed. [0003] Far-infrared rays generally refer to a section of electromagnetic waves with a wavelength of 4 μm to 400 μm in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/00B28C1/16B28B3/00
Inventor 金成洙
Owner 延吉可喜安医疗器械有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com