Process for preparing chromatic ceramics

A preparation technology and ceramic technology, which is applied in the field of color ceramic preparation technology, can solve the problems of dull, old-fashioned and monotonous ceramic color, and achieve the effect of good three-dimensional visual effect, obvious effect and rich color changes

Inactive Publication Date: 2010-02-10
李竹玲
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Ceramics are a great invention of the Chinese clan, and ceramic handicrafts are exquisite and exquisite. Yaozhou celadon was produced in Huangbao Town, Tongchuan, flourished in Tang Dynasty, flourished in Song Dynasty, and was destroyed in Yuan Dynasty. , is one of the most brilliant pearls in the history and culture of Tongchuan. The glaze color of Yaozhou celadon is superior to olive green and flashing yellow. The main tone is green, which is a cool color. With the constant change of people's aesthetics, the original ceramics are dull in color and appear monotonous, old and old-fashioned.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A preparation process of colored ceramics, characterized in that: the preparation process steps of the colored ceramics are:

[0020] ①. Raw material proportioning to make tire material; ②. Making mud molding material;

[0021] ③. Draw patterns and engrave flowers; ④. Mix and match colored mud to make tire materials;

[0022] ⑤. Fill in colored clay; ⑥. Biscuit firing to 800°C;

[0023] ⑦, applying transparent glaze; ⑧, firing into shape.

[0024] The raw material composition and parts by weight of the step ① are: 35 parts of Shangdian crucible, 20 parts of Yucai crucible, 25 parts of Yangping crucible, 10 parts of electric porcelain clay, and 5 parts of Baimiao crucible.

[0025] The raw material composition and parts by weight of the step ④ are: 20 parts of Dongshan crucible soil, 25 parts of Shangdian crucible soil, 5 parts of Lidipo crucible soil, 15 parts of Jingdezhen clay, 10 parts of Baimiao crucible, 10 parts of feldspar, 10 parts of quartz, 15 parts of coppe...

Embodiment 2

[0032] A preparation process of colored ceramics, characterized in that: the preparation process steps of the colored ceramics are:

[0033] ①. Raw material proportioning to make tire material; ②. Making mud molding material;

[0034] ③. Draw patterns and engrave flowers; ④. Mix and match colored mud to make tire materials;

[0035] ⑤. Fill in colored clay; ⑥. Biscuit firing to 800°C;

[0036] ⑦, applying transparent glaze; ⑧, firing into shape.

[0037] The raw material composition and parts by weight of the step ① are: 40 parts of Shangdian crucible, 20 parts of Yucai crucible, 20 parts of Yangping crucible, 15 parts of electric porcelain clay, and 5 parts of Baimiao crucible.

[0038] The raw material composition and parts by weight of the step ④ are: 26 parts of Dongshan crucible soil, 20 parts of Shangdian crucible soil, 10 parts of Lidipo crucible soil, 14 parts of Jingdezhen clay, 14 parts of Baimiao crucible, 8 parts of feldspar, 10 parts of quartz, 12 parts of coppe...

Embodiment 3

[0045] A preparation process of colored ceramics, characterized in that: the preparation process steps of the colored ceramics are:

[0046] ①. Raw material proportioning to make tire material; ②. Making mud molding material;

[0047] ③. Draw patterns and engrave flowers; ④. Mix and match colored mud to make tire materials;

[0048] ⑤. Fill in colored clay; ⑥. Biscuit firing to 800°C;

[0049] ⑦, applying transparent glaze; ⑧, firing into shape.

[0050] The raw material composition and parts by weight of the step ① are: 38 parts of Shangdian crucible, 23 parts of Yucai crucible, 23 parts of Yangping crucible, 13 parts of electric porcelain clay, and 8 parts of Baimiao crucible.

[0051] The raw material composition and parts by weight of the step ④ are: 25 parts of Dongshan crucible soil, 23 parts of Shangdian crucible soil, 8 parts of Lidipo crucible soil, 13 parts of Jingdezhen mud, 8 parts of Baimiao crucible, 8 parts of feldspar, 13 parts of quartz, 13 parts of copper o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of ceramics, in particular to a process for preparing chromatic ceramics. In recent years, cold-toned celadon products can not meet the requirement of modern people because of the enhancement of the living level and the change of the appreciation concept of people and the abundance of market substances. The process for preparing the chromatic ceramics comprises the following steps: (1) proportioning raw materials to prepare glaze materials; (2) preparing slurry molding materials; (3) drawing figures and engraving ; (4) proportioning chromatic slurryto prepare glaze materials; (5) filling the chromatic slurry; (6) carrying out bisque firing to 800 DEG C; (7) applying transparent glaze; and (8) firing and forming; preparing an artwork of the chromatic ceramics according to the technological steps by a certain mixture ratio of the raw materials. The ceramics prepared by the invention has abundant changes of figures and colors which more approach to the effect of a substance, and has hierarchy and good visual effect of three-dimension.

Description

technical field [0001] The invention belongs to the technical field of ceramics, and in particular relates to a preparation process of colored ceramics. Background technique [0002] Ceramics are a great invention of the Chinese clan, and ceramic handicrafts are exquisite and exquisite. Yaozhou celadon was produced in Huangbao Town, Tongchuan, flourished in Tang Dynasty, flourished in Song Dynasty, and was destroyed in Yuan Dynasty. , is one of the most brilliant pearls in the history and culture of Tongchuan. The glaze color of Yaozhou celadon is superior to olive green and flashing yellow. The main tone is green, which is a cool color. With the constant change of people's aesthetics, the original ceramics are dim in color, appearing monotonous, old and old-fashioned. Contents of the invention [0003] The object of the present invention is to provide a process step for the preparation of colored ceramics with rich patterns and colors and obvious effects. [0004] Techn...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/00
Inventor 李竹玲任栓民
Owner 李竹玲
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com