Preparation method of PBT silver-ion antibiotic moisture-absorption deodorization fibre

A silver ion and fiber technology is applied in the field of preparation of PBT silver ion antibacterial, moisture-absorbing and deodorizing fibers, which can solve problems such as no reports on PBT silver-ion antibacterial, moisture-absorbing and deodorizing fibers, and achieve excellent chemical resistance, good durability, Good durability

Inactive Publication Date: 2010-06-30
YIZHENG XINGHAI CHEM FIBER
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] There is no report of relevant PBT silver ion antibacterial, moisture-absorbing and deodorizing fibers in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of PBT silver-ion antibiotic moisture-absorption deodorization fibre
  • Preparation method of PBT silver-ion antibiotic moisture-absorption deodorization fibre

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0013] In conjunction with accompanying drawing, the preparation method of a kind of PBT silver ion antibacterial hygroscopic deodorant fiber of the present invention comprises the following steps:

[0014] Step 1. Pre-crystallize the material, which is a mixture of PBT slices and silver ion SHT antibacterial plastic masterbatch; specifically, dry hot air is used for pre-crystallization; when the material is pre-crystallized, the pre-crystallization temperature is 120-125°C , The temperature of the dry hot air is 130-135°C, the air dew point is less than or equal to -60°C, the moisture content of the material is 30ppm, and the drying time is 8-10 hours.

[0015] Step 2. Material screw feeding: first dry the color masterbatch with hot air, then feed the mixed material of the color masterbatch and PBT chips into the screw extruder through a special color masterbatch feeder that can measure the color masterbatch Middle; when the material is screw-fed, the material is a mixture of...

Embodiment 1

[0020] A preparation method of PBT silver ion antibacterial, moisture-absorbing and deodorant fiber, comprising the following steps:

[0021] Step 1. Pre-crystallize the material, which is a mixture of PBT slices and silver ion SHT antibacterial plastic masterbatch; specifically, dry hot air is used for pre-crystallization; when the material is pre-crystallized, the pre-crystallization temperature is 120 ° C, and the The temperature of the hot air is 130°C, the air dew point is -60°C, the moisture content of the material is 30ppm, and the drying time is 8 hours.

[0022] Step 2. Material screw feeding: first dry the color masterbatch with hot air, then feed the mixed material of the color masterbatch and PBT chips into the screw extruder through a special color masterbatch feeder that can measure the color masterbatch Middle; when the material is screw-fed, the material is a mixture of PBT (polybutylene terephthalate) slices and silver ion SHT (nano silver inorganic antibacter...

Embodiment 2

[0026] A preparation method of PBT silver ion antibacterial, moisture-absorbing and deodorant fiber, comprising the following steps:

[0027] Step 1. Pre-crystallize the material, which is a mixture of PBT slices and silver ion SHT antibacterial plastic masterbatch; specifically, dry hot air is used for pre-crystallization; when the material is pre-crystallized, the pre-crystallization temperature is 125 ° C, and the drying The temperature of the hot air is 135°C, the air dew point is -55°C, the moisture content of the material is 30ppm, and the drying time is 10 hours.

[0028] Step 2. Material screw feeding: first dry the color masterbatch with hot air, then feed the mixed material of the color masterbatch and PBT chips into the screw extruder through a special color masterbatch feeder that can measure the color masterbatch Middle; when the material is screw-fed, the material is a mixture of PBT (polybutylene terephthalate) slices and silver ion SHT (nano silver inorganic an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of PBT silver-ion antibiotic moisture-absorption deodorization fibre, which comprises the following steps of: (1) crystallizing a material in advance, wherein the material is the mixture of a PBT slice and a silver-ion SHT antibiotic plastic master batch; concretely, crystallizing in advance by adopting dry hot air; (2) feeding the material in a screw type: firstly, drying the master batch by the hot air and then feeding the material obtained after mixing the master batch and the PBT slice into a screw extruder by a special master batch feeding machine which can measure the master batch; (3) filtering: filtering the mixture extruded by the extruder wherein the continuous production of spinning and the constancy of the pressure of the screw extruder are ensured during filtering; and (4) spinning: delivering the mixture from the filter to a spinning assembly, ejecting from a spinneret plate by the spinning assembly, and then coiling and forming. The fibre has favorable durability, dimensional stability and better elasticity, and the elasticity is free from the influence of the humidity.

Description

technical field [0001] The invention belongs to the technical field of fiber preparation, in particular to a method for preparing a PBT silver ion antibacterial, moisture-absorbing and deodorizing fiber. Background technique [0002] Many metal ions have bactericidal and anti-mildew effects. The antibacterial mechanism is generally divided into two categories: one is to destroy the structure of bacteria, and the other is to affect metabolism and physiological activities. Silver ions can kill bacteria by destroying the plasma membrane of bacteria. In addition, silver ions can destroy the three-dimensional conformation of proteases by combining with the sulfhydryl group (-SH) of proteins and kill microorganisms. Therefore, silver fibers (silver ions) provide dual functions of antibacterial and deodorizing. Bacterial growth will cause body odor. Coincidentally, qualitatively altered proteins will also produce odor on clothes and socks. The silver component on the surface of s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01D5/10D01D5/253D01D1/10D01F6/92
Inventor 周仁忠
Owner YIZHENG XINGHAI CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com