A production method and anti-aging technology, applied in heating/cooling fabrics, textiles and papermaking, fabric surface trimming, etc., can solve the problems of environmental pollution by organic matter volatilization, high energy consumption and high production costs, and achieve easy recycling and long service life. Long, low production cost effect

Inactive Publication Date: 2010-08-04
SICHUAN UNIV
View PDF5 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method can be used to produce glass fiber cloth, asphalt waterproof membrane and other products, but it has the problems of volatile organic matter polluting the environment and high energy consumption
The lamination method is a method of laminating the pre-made PVC film and the substrate on the laminator to obtain artificial leather. This method has many production processes, and the plastic film needs to be processed first, and then the lamination is carried out. The energy consumption is large and the production cost is high. high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Put 0.56 parts of aminosilane diluted in ethanol, 15 parts of 50 mesh hollow glass microspheres, 10 parts of 40 mesh ferric oxide, and 3 parts of 1000 mesh carbon black into a high-speed mixer and mix for 8 minutes before unloading, then Put the mixed material into a fluidized fluidized bed, and keep the temperature at 80-85°C for 2 hours to form a coating on the surface of the thermal insulation material; mix 100 parts of low-density polyethylene, the treated thermal insulation material, 0.3 parts of antioxidant 1010, 0.3 1 part of antioxidant TNPP, 0.2 part of light stabilizer 744 and 3 parts of maleic anhydride grafted polyethylene were placed in a high-speed mixer, and after mixing for 5 minutes, they were added to a twin-screw extrusion casting coating machine for melt plasticization and extrusion , at a melt temperature of 195°C, it is cast and coated on the continuously advancing ultra-high molecular weight polyethylene fiber fabric base, and then cooled with a co...

Embodiment 2

[0039] Put 0.34 parts of vinyltriethoxysilane diluted in ethanol, 10 parts of 80-mesh hollow microspheres, 5 parts of nano-antimony tin oxide, and 2 parts of 1000-mesh carbon black into a high-speed mixer and mix for 8 minutes before unloading , and then put the mixed material into a hot air oven, and keep the temperature at 80-85°C for 3 hours to form a coating on the surface of the heat insulating material; mix 100 parts of linear low density polyethylene, the treated heat insulating material, 0.2 parts of antioxidant 1076, Put 0.3 part of DLTP, 0.1 part of light stabilizer 2002, 4 parts of glycidyl acrylate grafted polyethylene and 1 part of PE wax into a high-speed mixer, mix to a temperature of 105°C, and add twin-screw extrusion casting coating It is melted and plasticized and extruded in the machine, cast and coated on the continuously advancing polypropylene fiber fabric cloth base at a melt temperature of 210°C, and then cooled with a cooling roll at 80-85°C for shapin...

Embodiment 3

[0042] Put 0.64 parts of epoxy silane diluted in ethanol, 10 parts of 80-mesh airgel silica, 10 parts of 50-mesh hollow alumina balls, and 6 parts of nano-sized rutile titanium dioxide into a high-speed mixer and mix for 8 Unload the material after 10 minutes, then put the mixed material into the drying incubator, and keep the temperature at 80-85°C for 3 hours to form a coating on the surface of the thermal insulation material; mix 100 parts of high-density polyethylene, treated thermal insulation material, 0.5 parts of anti-corrosion Oxygen agent 300, 0.1 part of UV-327, 0.3 part of PL-10 and 1 part of PE wax are put into a high-speed mixer, mixed to a temperature of 105°C, then added to a twin-screw extrusion casting coating machine for melt plasticization and extrusion , at a melt temperature of 230°C, it is cast and coated on the continuously advancing ultra-high molecular weight polyethylene fiber fabric base, and then cooled with a cooling roller at 105-115°C for shaping...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
barrier rateaaaaaaaaaa
Login to view more

Abstract

The invention discloses an ageing-resistant heat-insulation tarpaulin. The tarpaulin is composed of a polymer cloth base and an ageing-resistant heat-insulation coating which is coated on the polymer cloth base in a casting mode. After aging is quickened for 236 hours by simulating natural manual work, the tensile strength of the tarpaulin is improved by at least 10%, the elongation at break thereof is improved by at least 5% than the elongation at break before aging, the ultraviolet reflectivity thereof is more than or equal to 80%, and the infrared obstruction rate thereof is more than or equal to 85%. The invention also discloses a preparation method thereof, comprising the following step: pretreating a heat-insulation material by utilizing a surface treating agent; and premixing the heat-insulation material with accessory ingredients such as vinyl type polymer, antioxidant and the like, then putting the heat-insulation material and the accessory ingredients into a double-screw extrusion casting coating machine to be fused, plasticized and extruded out to be casted and coated on the polymer fiber cloth base, and carrying out cooling shaping and reeling by utilizing a cooling roll to obtain the ageing-resistant heat-insulation tarpaulin. The tarpaulin product obtained by the invention has favourable water proofness, heat-insulating property and ageing-resistant property, wide application range, no pollution in the production process, small energy consumption, low cost and easy popularization and application.

Description

technical field [0001] The invention belongs to the technical field of tarpaulin products and production methods thereof, and in particular relates to a tarpaulin with anti-aging heat insulation performance prepared by extrusion casting and coating a cloth base and a production method thereof. Background technique [0002] Tarpaulin, also known as coated cloth, is a waterproof product made of polymer coated on the cloth base, mainly used in occasions that require waterproof, dustproof and barrier. Specifically, it can be used as clothing, labor protection supplies, logistics packaging, tarpaulins for automobiles, tents for travel and living, and waterproofing for building roofs. [0003] Common tarpaulins include PVC flame-retardant waterproof tarpaulin, polyester waterproof tarpaulin, polypropylene waterproof tarpaulin, asphalt waterproof membrane, etc. Polyvinyl chloride flame-retardant waterproof tarpaulin is a coated cloth composed of double-sided coated polyvinyl chlor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/00D06B1/04D06C7/02
Inventor 吴智华胡贵张清松孟兵熊鸿
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap