Damping wear-resistant aluminum alloy material and preparation method thereof

An aluminum alloy material and aluminum alloy technology, applied in the field of metal materials, can solve the problems of low comprehensive performance of ordinary aluminum alloy wear resistance and damping, complicated preparation process, etc., and achieve industrial production convenience, simple preparation process, and production low cost effect

Inactive Publication Date: 2011-05-11
金湖中博物联网科技有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The comprehensive properties of wear resistance and damping of the above ordinary aluminum alloys are not high, and the preparation process is complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Damping wear-resistant aluminum alloy material and preparation method thereof
  • Damping wear-resistant aluminum alloy material and preparation method thereof
  • Damping wear-resistant aluminum alloy material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The weight percentage of the chemical composition of the aluminum alloy matrix: Mg is 0.1%, Zr is 0.2%, Si is 5%, Pb is 2%, Sn is 1%, La is 0.05%, Ho is 0.01%, and the rest is Al .

[0034] The weight percentage of the chemical composition of the steel wire: C is 0.45%, Si is 0.2%, Mn is 0.5%, P<0.02%, S <0.025%, and the rest is Fe; the cross section of the steel wire is rectangular, and the specification is 0.1mm ×0.5mm.

[0035] The carbon fiber is T300 with a diameter of 7 microns and an aspect ratio of 100:1.

[0036] The weight ratio of the steel wire and the carbon fiber is 25:1, and the volume percentage of the control steel wire and the carbon fiber is 20% of the material.

[0037] Get steel wire and form the steel wire group of clean ball shape according to the conventional method of cleaning ball or steel ball production, the diameter of steel wire group is 10cm, and obtain the cobalt-coated steel wire group at its surface cobalt-plated according to the meth...

Embodiment 2

[0042] The weight percentage of the chemical composition of the aluminum alloy matrix: Mg is 0.3%, Zr is 0.5%, Si is 7%, Pb is 3%, Sn is 2%, La is 0.1%, Ho is 0.03%, and the rest is Al .

[0043] The weight percentage of the chemical composition of the steel wire: C is 0.65%, Si is 0.3%, Mn is 0.85%, P<0.02%, S <0.025%, and the rest is Fe; the cross section of the steel wire is rectangular, and the specification is 0.4mm ×1.5mm.

[0044] The carbon fiber is T300 with a diameter of 7 microns and an aspect ratio of 400:1.

[0045] The weight ratio of steel wire and carbon fiber is 30:1, and the volume percentage of the control steel wire and carbon fiber is 40% of the material.

[0046] Get steel wire and form the steel wire group of cleaning ball shape according to the conventional method of cleaning ball or steel ball production, the diameter of steel wire group is 15cm, and obtain the cobalt-coated steel wire group at its surface cobalt-plated according to the method for ro...

Embodiment 3

[0049] The chemical composition of the aluminum alloy matrix is ​​0.2% by weight of Mg, 0.4% of Zr, 6% of Si, 2.5% of Pb, 1.5% of Sn, 0.07% of La, 0.02% of Ho, and the rest is Al.

[0050] The weight percentage of the chemical composition of the steel wire: C is 0.5%, Si is 0.25%, Mn is 0.7%, P<0.02%, S <0.025%, and the rest is Fe; the cross section of the steel wire is rectangular, and the specification is 0.3mm ×0.7mm.

[0051] The carbon fiber is T300 with a diameter of 7 microns and an aspect ratio of 190:1.

[0052] The weight ratio of steel wire and carbon fiber is 27:1, and the volume percentage of the control steel wire and carbon fiber is 35% of the material.

[0053] Get steel wire and form the steel wire group of cleaning ball shape according to the conventional method of cleaning ball or steel ball production, the diameter of steel wire group is 12cm, and obtain the cobalt-coated steel wire group at its surface cobalt plating according to the conventional chemical...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a damping wear-resistant aluminum alloy material and a preparation method thereof. In the damping wear-resistant aluminum alloy material, aluminum alloy serves as a matrix; steel wire rolls and carbon fibers are distributed in the matrix; the diameter of each steel wire roll is 10 to 15 centimeters; each steel wire has a rectangular section and the section size is 0.1-0.4 mm*0.5-1.5 mm; the weight ratio of the steel wires to the carbon fibers is 25-30:1; and the steel wires and the carbon fibers account for 20 to 40 percent of the volume of the material. The damping wear-resistant aluminum alloy material prepared by the method has high toughness, wear resistance, a simple process and low production cost.

Description

technical field [0001] The invention belongs to the field of metal materials, and in particular relates to a steel wire and carbon fiber composite reinforced damping wear-resistant aluminum alloy material and a preparation method thereof. Background technique [0002] In the field of metal materials, damping and wear-resistant aluminum alloys have been widely valued as wear-resistant materials. [0003] Application No. CN200610165341.X discloses a high-strength damping and wear-resistant aluminum alloy and its preparation method. The high-strength damping and wear-resistant aluminum alloy is placed in a Ti-C-Al prefabricated block in an Al-Zn-Mg-Cu alloy melt , through the in-situ reaction to generate TiC particles in the Al-Zn-Mg-Cu alloy melt, and then carry out atomization spray forming, wherein, the TiC insertion amount of the Ti-C-Al prefabricated block is Al-Zn- 3.15 to 10.5% (weight %) of the Mg-Cu alloy. The preparation method is as follows: (1) press Ti powder, gr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C49/06C22C49/14C22C47/08C22C47/04C22C47/02C22C111/00C22C101/10C22C121/02C22C121/00
Inventor 赵浩峰王玲雷勇
Owner 金湖中博物联网科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap