600HB-grade wear resistant steel plate and its manufacturing method

A wear-resistant steel plate and a manufacturing method technology, applied in the field of wear-resistant steel, can solve the problems of deteriorating welding and processing performance of wear-resistant steel, and achieve the effects of eliminating internal stress, loose process system, and reasonable composition and process design.

Active Publication Date: 2012-09-19
BAOSHAN IRON & STEEL CO LTD
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Large amounts of carbon and alloy content can seriously deteriorate the welding and machining properties of wear-resistant steels

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 600HB-grade wear resistant steel plate and its manufacturing method
  • 600HB-grade wear resistant steel plate and its manufacturing method
  • 600HB-grade wear resistant steel plate and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] The chemical composition of the 600HB wear-resistant steel plate of the present invention is shown in Table 2. According to the chemical composition shown in Table 2, it is smelted in an electric furnace or a converter. After refining, it is cast into a continuous casting billet or ingot. The continuous casting billet or steel ingot is heated to 1250 ° C, the rolling temperature is 1200 ° C, and the thickness of the finished steel plate is 6mm. After rolling Air cooling, quenching heating temperature is Ac 3 +80°C, tempering temperature is 300°C, after tempering, stacking or cooling bed cooling.

Embodiment 2

[0047] The implementation is the same as in Example 1, wherein the heating temperature is 1230°C, the rolling start temperature is 1180°C, the thickness of the finished steel plate is 12mm, and the quenching heating temperature is Ac 3 +60°C, tempering temperature is 250°C, after tempering, stack or cool down in a cooling bed.

Embodiment 3

[0049] The implementation method is the same as in Example 1, wherein the heating temperature is 1200°C, the rolling start temperature is 1150°C, the thickness of the finished steel plate is 20mm, and the quenching heating temperature is Ac 3 +50°C, tempering temperature is 220°C, after tempering, stack or cool down in a cooling bed.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Brinell hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

Disclosed is a 600HB-grade wear resistant steel plate, comprising, by weight, 0.41 to 0.50% of C, 0.10 to 0.60% of Si, 0.20 to 1.20% of Mn, no more than 0.050% of P, no more than 0.030% of S, 0.01 to 1.50% of Cr, 0.01 to 1.00% of Mo, 0.01 to 1.50% of Ni, 0.001 to 0.10% of Ti, 0.001 to 0.10% of Al, 0.001 to 0.10% of RE, 0.01 to 1.00% of W, 0.0005 to 0.0040% of B, 0.001 to 0.010% of Ca, the balanceFe and unavoidable impurities. The 600HB-grade wear resistant steel plate provided in the invention has high hardness (no less than 600HB), good toughness and plasticity, high abrasion resistance andexcellent processability and weldability; the microstructure is martensite or martensite and retained austenite. Therefore, the 600HB-grade wear resistant steel plate is extremely suitable for being used in high abrasion environment, especially for being used in vehicles or equipment which contact with such materials of high hardness as high strength ores, for example, a bucket, or the compartment of an electric wheel self-discharging truck for mining, etc.

Description

technical field [0001] The invention relates to wear-resistant steel, in particular to a 600HB wear-resistant steel plate and a manufacturing method thereof. Background technique [0002] In the case of particularly harsh working conditions, it is necessary to use strong and high-hardness wear-resistant steel plates to reduce the wear of the equipment and prolong its service life. [0003] The wear resistance of a material mainly depends on its hardness, and the toughness also has a certain influence. The higher the strength and hardness of wear-resistant steel, the higher its carbon and alloy content, and the poorer its welding performance. At the same time, the performance of cutting and bending is also poor, which limits the wide application of high-hardness wear-resistant steel in engineering. [0004] Most of the existing wear-resistant steels are high-carbon wear-resistant steels. As disclosed in Chinese patent CN1099810, the maximum carbon content is as high as 1.20...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/54C21D8/02C21D1/18
Inventor 李红斌姚连登刘自成赵小婷
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com