Foaming agent for sound absorption foam concrete product and preparation method for foaming agent

A technology for concrete products and sound-absorbing foam, which is applied in the field of foaming agents, can solve the problems affecting the performance of sound-absorbing products and the sound-absorbing effect is not ideal, and achieves the effects of better sound-absorbing effect, stable bubbles, and simple preparation process.

Inactive Publication Date: 2013-05-08
梁材
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there is no foaming material specially designed for the preparation of sound-absorbing foamed concrete products on the market. The sound-absorbing effect of sound-absorbing foamed concrete products prepared by ordinary foaming materials is not ideal. What is more serious is that some foaming agents are still It affects other properties of sound-absorbing products, such as strength, etc. Many of the above factors restrict the further promotion and popularization of sound-absorbing foam concrete products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Foaming agent for sound absorption foam concrete product and preparation method for foaming agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] According to the mass ratio, it is fatty alcohol polyoxyethylene ether sodium sulfate (AES) 5-7%, sodium dodecyl sulfate (K12) 1%, sodium dodecylbenzenesulfonate (DBS) 3.5%, tea saponin 0.15% %, disodium ethylenediaminetetraacetic acid (EDTA) 2%, modified nano-bentonite 1.5% and the rest of the water to prepare raw materials. First add fatty alcohol polyoxyethylene ether sodium sulfate (AES) into an appropriate amount of water, heat and stir evenly in a water bath at a temperature of 30°C-50°C; then add sodium lauryl sulfate (K12), dodecylbenzene Sodium sulfonate (DBS), continue to stir until all materials are completely dissolved, and finally add tea saponin, disodium ethylenediaminetetraacetic acid (EDTA), modified nano-bentonite and the rest of the water.

Embodiment 2

[0027] According to the mass ratio, it is fatty alcohol polyoxyethylene ether sodium sulfate (AES) 5.5-7.5%, sodium dodecyl sulfate (K12) 2%, sodium dodecylbenzenesulfonate (DBS) 2.5%, tea saponin 0.3 %, disodium ethylenediaminetetraacetic acid (EDTA) 2.5%, modified nano-bentonite 2% and the rest of the water to prepare raw materials. First add fatty alcohol polyoxyethylene ether sodium sulfate (AES) into an appropriate amount of water, heat and stir evenly in a water bath at a temperature of 30°C-50°C; then add sodium lauryl sulfate (K12), dodecylbenzene Sodium sulfonate (DBS), continue to stir until all materials are completely dissolved, and finally add tea saponin, disodium ethylenediaminetetraacetic acid (EDTA), modified nano-bentonite and the rest of the water.

Embodiment 3

[0029] According to the mass ratio, it is fatty alcohol polyoxyethylene ether sodium sulfate (AES) 7-8%, sodium dodecyl sulfate (K12) 3%, sodium dodecylbenzenesulfonate (DBS) 1.5%, tea saponin 0.45% %, disodium ethylenediaminetetraacetic acid (EDTA) 3%, modified nano-bentonite 2.5% and the rest of the water to prepare raw materials. First add fatty alcohol polyoxyethylene ether sodium sulfate (AES) into an appropriate amount of water, heat and stir evenly in a water bath at a temperature of 30°C-50°C; then add sodium lauryl sulfate (K12), dodecylbenzene Sodium sulfonate (DBS), continue to stir until all materials are completely dissolved, and finally add tea saponin, disodium ethylenediaminetetraacetic acid (EDTA), modified nano-bentonite and the rest of the water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a foaming agent for a sound absorption foam concrete product and a preparation method for the foaming agent. The foaming agent comprises the following components in percentage by mass: 5 to 10 percent of fatty alcohol-polyoxyethylene ether sodium sulfate, 1 to 5 percent of lauryl sodium sulfate, 1 to 5 percent of sodium dodecyl benzene sulfonate, 0.1 to 2 percent of tea saponin, 1 to 5 percent of disodium ethylene diamine tetraacetate, 1 to 5 percent of modified nanometer bentonite and the balance of water. The foaming agent special for sound absorption foam concrete is stable in performance, high in foaming times and high in workability with concrete base materials, and has an adjustable pore structure.

Description

technical field [0001] The invention relates to a foaming agent, in particular to a foaming agent for sound-absorbing foam concrete products and a preparation method thereof. Background technique [0002] At present, urbanization is in full swing, with the rapid development of various means of transportation and the densification of population, a series of noise problems resulting from this have seriously affected the normal life of human beings. At the same time, sound-absorbing and sound-insulating materials Also facing new development opportunities, sound-absorbing products of various materials have sprung up like mushrooms after rain, and sound-absorbing foam concrete products are the best of these materials. [0003] At present, there is no foaming material specially designed for the preparation of sound-absorbing foamed concrete products on the market. The sound-absorbing effect of sound-absorbing foamed concrete products prepared by ordinary foaming materials is not i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/02C04B24/20
Inventor 梁材
Owner 梁材
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap