Aluminium Alloy Plate For Cell Box And Cell Box

An aluminum alloy plate and battery box technology, applied in battery pack parts, circuits, electrical components, etc., can solve the adverse effects of electrical conductivity and working voltage performance, reduce the shape stability of welding beads, and increase the incidence of irregular welding beads. and other problems, to achieve the effect of excellent pulsed laser weldability and excellent formability

Inactive Publication Date: 2015-05-06
KOBE STEEL LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in JISA3003 aluminum alloy, if the depth of penetration exceeds 0.25mm, the shape stability of the weld bead will be significantly reduced, and the incidence of irregular weld bead will increase sharply.
Depending on the situation, this irregular bead may cause penetration into the back of the material to be welded, causing problems that adversely affect performance such as electrical conductivity and operating voltage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminium Alloy Plate For Cell Box And Cell Box
  • Aluminium Alloy Plate For Cell Box And Cell Box
  • Aluminium Alloy Plate For Cell Box And Cell Box

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0076][Preparation of test materials]

[0077] The aluminum alloys shown in Table 3 were subjected to the same manufacturing process as in Example 1 to obtain an aluminum alloy plate with a plate thickness of 10 mm. 【table 3】

[0078]

mn

Cu

Mg

Si

Fe

Zn

Ti

B*

Al

Example 3

0.82

0.15

-

0.11

0.62

0.01

0.003

9.1

margin

Example 4

0.97

0.15

-

0.11

0.64

0.01

0.003

9.6

margin

Example 5

1.42

0.15

-

0.12

0.66

0.01

0.004

9.7

margin

Example 6

0.96

0.07

-

0.11

0.65

0.01

0.003

9.3

margin

Example 7

0.98

0.14

-

0.07

0.61

0.01

0.003

9.6

margin

Example 8

1.00

0.15

-

0.56

0.68

0.01

0.004

9.8

margin

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

When carrying out pulse laser welding over JISA3000 aluminium alloy plate for a cell box, the abnormal part (irregular weld pass) can be avoided. The aluminium alloy plate for a cell boxy comprises, by mass, 0.8 to 1.5% of Mn, 0.05 to 0.2% of Cu, 0.05 to 0.6% of Si, and 0.05 to 0.7% of Fe. According to the requirement, by mass, Zn is below 0.05%, Ti below 0.04, and B below 10 ppm. The remains are constituted by A1 and some unavoidable impurity. Even when the penetration depth of the laser is over 0.25mm, the irregular weld pass can still be avoided.

Description

technical field [0001] The present invention relates to an aluminum alloy plate for battery boxes used in lithium ion secondary battery boxes and the like, and the battery box. Background technique [0002] Lithium-ion secondary batteries are widely used as batteries for mobile phones, notebook personal computers, and the like. Among the materials for the case (hereinafter referred to as the battery box as appropriate) of the secondary battery, conventionally, for the purpose of reducing the size and weight of the battery, there are also materials used for forming the battery box (mainly the battery box body) The property (formability) is good, and the aluminum alloy material is used. [0003] In batteries for mobile phones and notebook computers, swelling of the battery becomes a problem. Therefore, in order to obtain high strength, an alloy in which a large amount of Cu and Mg is added using an Al—Mn-based alloy as a base material has been developed (see Patent Document ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/00H01M2/02B23K26/32H01M2/04
CPCY02E60/10C22C21/00B23K26/32H01M50/147H01M50/119
Inventor 小林一德松本刚
Owner KOBE STEEL LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com