Mineral polyurethane spraying material and preparation method thereof

A spraying material, polyurethane technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of many construction workers, high labor intensity, dry cracking of urea-formaldehyde resin, etc., and achieve high strength of the consolidated body, easy to use, good toughness Effect

Active Publication Date: 2012-07-04
SHANDONG INOV NEW MATERIALS CO LTD
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Spraying mortar seriously pollutes underground, requires more construction workers, labor intensity is high, and work efficiency is low
Phenolic resin and urea-formaldehyde resin contain formaldehyde, which is irritating and toxic to construction workers, and phenolic resin emits a large amount of harmful gas when exposed to high temperature, and urea-formaldehyde resin will dry out and fall off after a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mineral polyurethane spraying material and preparation method thereof
  • Mineral polyurethane spraying material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Prepare 100 kilograms of component A materials, weighing respectively: polyether polyol A (6 functionalities, molecular weight is 800) 42 kilograms, polyether polyol B (4 functionalities, molecular weight is 600) 23 kilograms, polyester polyol C (2 functionality, molecular weight is 340) 2 kilograms, polyester polyol D (2 functionality, molecular weight is 300) 2 kilograms, catalyst 1,3,5-tris(dimethylaminopropyl) hexahydrotriazine 0.5 kg, catalyst dibutyltin dilaurate 0.7 kg, catalyst N, N, N', N", N"-pentamethyldiethylenetriamine 0.1 kg, water 1.2 kg, L-6950 1.5 kg, monofluorodichloro 16 kg of ethane, 11 kg of trichloropropyl phosphate. Put the weighed polyether polyol and polyester polyol into the mixing tank and stir, then add the weighed catalyst, water, stabilizer, and foaming agent respectively, and stir evenly at room temperature. After sampling and testing are qualified, you can barreled.

[0034] Component B is polyphenyl polymethylene polyisocyanate.

[00...

Embodiment 2

[0040] Prepare 100 kilograms of component A materials, weigh respectively: polyether polyol A (6 functionalities, molecular weight is 800) 45 kilograms, polyether polyol B (4 functionalities, molecular weight is 600) 25 kilograms, polyester polyol C (2 functionality, molecular weight is 340) 2 kilograms, polyester polyol D (2 functionality, molecular weight is 300) 3 kilograms, catalyst 1,3,5-tris(dimethylaminopropyl) hexahydrotriazine 0.3 kg, catalyst dibutyltin dilaurate 0.7 kg, catalyst N, N, N', N", N"-pentamethyldiethylenetriamine 0.1 kg, water 1.4 kg, L-6950 1.5 kg, monofluorodichloro 10 kg of ethane, 11 kg of trichloropropyl phosphate. Put the weighed polyether polyol and polyester polyol into the mixing tank and stir, then add the weighed catalyst, water, stabilizer, and foaming agent respectively, and stir evenly at room temperature. After sampling and testing are qualified, you can barreled.

[0041] Component B is polyphenyl polymethylene polyisocyanate.

[0042]...

Embodiment 3

[0047] Prepare 100 kilograms of component A materials, weighing respectively: 40 kilograms of polyether polyol A (6 functionality, molecular weight is 880), 20 kilograms of polyether polyol B (4.0 functionality, molecular weight is 600), polyester polyol C (2 functionality, molecular weight is 340) 2 kilograms, polyester polyol D (2 functionality, molecular weight is 300) 3 kilograms, catalyst 1,3,5-tris(dimethylaminopropyl) hexahydrotriazine 0.5 kg, 0.7 kg of dibutyltin dilaurate, catalyst N, N, N', N", N"-pentamethyldiethylenetriamine 0.1 kg, water 1.4 kg, L-6950 1.3 kg, monofluorodichloroethyl 21 kilograms of alkane, 11 kilograms of trichloropropyl phosphate. Put the weighed polyether polyol and polyester polyol into the mixing tank and stir, then add the weighed catalyst, water, stabilizer, and foaming agent respectively, and stir evenly at room temperature. After sampling and testing are qualified, you can barreled.

[0048] Component B is polyphenyl polymethylene polyi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of chemical synthesis, particularly relates to a mineral polyurethane spraying material and a preparation method thereof and more particularly relates to a double-component (A and B) polyurethane material and a preparation method thereof. The material is mainly used for rapidly spraying and sealing underneath mine; and through the selection of polyol, auxiliaries and isocyanate, the spraying material has good adhesion on a rock coal body; and after adhesion is carried out, the material has good anti-shearing property and toughness and resists impact. According to the invention, the viscosity of the material is reduced so that the material can well permeate into a coal bed or a fine crack of a rock stratum, and simultaneously, the related raw materials are low in smell, do not contain volatile solvent and do not generate any toxic gases, thereby completely meeting the use and environment-friendly requirements of a coal mine reinforcement material.

Description

technical field [0001] The invention belongs to the field of chemical synthesis, and in particular relates to a mine-used polyurethane spraying material and a preparation method thereof. Background technique [0002] During the excavation process of the new coal mine roadway, the surface rocks are easily damaged by weathering, and accidents of falling rocks and people are prone to occur. Therefore, the surface of the roadway needs to be coated. By spraying and sealing the wall of the goaf, the air leakage and gas gushing out of the gob can be effectively prevented, and the occurrence of coal-oxygen compound heat release and coal seam fire can be prevented. In addition, spray the surface of masonry closed walls and coal wall joints to prevent carbon monoxide and gas leakage. [0003] At present, the treatment methods for mine roadway walls mainly include spraying mortar, phenolic resin, urea-formaldehyde resin, etc. Spraying mortar is seriously polluted underground, requiri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D175/08C09D175/06C09D7/12
Inventor 由明张丽郝德开
Owner SHANDONG INOV NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com