Transparent thermal insulation material and preparation method thereof

A heat-insulating material and transparent technology, applied in radiation-absorbing coatings, chemical instruments and methods, sustainable manufacturing/processing, etc., can solve problems such as complex manufacturing processes, and achieve long-term quality stability

Active Publication Date: 2012-08-22
NANYA PLASTICS CORP
View PDF8 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the manufacturing process of the composite tungsten oxide still has the disadva

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transparent thermal insulation material and preparation method thereof
  • Transparent thermal insulation material and preparation method thereof
  • Transparent thermal insulation material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0071] Mix tungsten hexachloride and ethanol to prepare a blue solution A with a pH value of about 0; additionally take cesium chloride (CsCl) and antimony trichloride (SbCl) 3 ) were mixed together with water in a ratio of 1 mole to 0.1 mole to prepare clear solution B. The two solutions of A and B were co-deposited to produce precipitates. The chemical reaction formula is as follows:

[0072] 2WCl 6 +C 2 h 5 OH+3H 2 O→WOCl 4 ↓+WO 2 Cl 2 ↓+6HCl+C 2 h 5 OH;

[0073] WOCl 4 ↓+WO 2 Cl 2 ↓+C 2 h 5 OH+CsCl+SbCl 3 +3H 2 O→2WO 3 ↓+Cs + +Sb +3 +Cl - +6HCl+C 2 h 5 Oh.

[0074] Next, the obtained precipitate was placed in a high-temperature furnace, and a certain flow rate of argon and hydrogen was introduced. Under the condition that the temperature increase rate of the high-temperature furnace was 2°C per minute, the high-temperature furnace was raised from room temperature to 485-485°C. 515°C (expressed as an average temperature of 500°C), and heat treatment...

Embodiment 2

[0080] With embodiment 1, but get cesium chloride and antimony trichloride (SbCl 3 ) were mixed together with water in a ratio of 1 mole to 0.5 mole to prepare clear solution B.

[0081] The transmittance of the prepared transparent heat-insulating film to a wavelength of 300-2000 nm was measured, and the results are listed in Table 1.

Embodiment 3

[0083] With embodiment 2, but use tin trichloride (SnCl 3 ) to replace antimony trichloride (SbCl 3 ) to prepare a transparent solution B.

[0084] The transmittance of the prepared transparent heat-insulating film to a wavelength of 300-2000nm was measured, and the results are listed in Table 1; the results of the life test trend chart are listed in figure 1 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a transparent thermal insulation material, which is characterized in that: the material is codoped by cross-group elements. A preparation method of the material has the characteristics of simple process and cost saving, and is specially used for preparing composite wolfram oxygen chloride powder with a chemical formula being CsxNyWO3-ZCIC, wherein Cs is cesium; N is Sn or Sb or Bi; W is wolfram; O is oxygen; and X, Y, Z and C are positive numbers and meet the following conditions that: X is less than or equal to 1.0, Y is less than or equal to 1.0, Y/X is less than or equal to 1.0, Z is less than or equal to 0.6, and C is less than or equal to 0.1. A transparent thermal insulation film prepared by the composite wolfram oxygen chloride powder has the characteristics of high transparency and high thermal insulation, is applied to paste on glasses of buildings and automobiles so as to separate infrared wave bands with wavelength of 800-2000nm, contributes to realizing effects of thermal insulation and energy conservation, and also can be used for a combined type base plate of an electronic component.

Description

technical field [0001] The invention relates to a transparent heat-insulating material and its preparation method, in particular to a transparent heat-insulating film made of the transparent heat-insulating material, which has both high transparency and excellent infrared barrier properties. Background technique [0002] In order to achieve the purpose of energy saving and carbon reduction, in the prior art, a layer of heat insulating material is usually pasted on the glass of buildings and automobiles to achieve the effect of heat insulation and energy saving. The physical properties of metal oxides have good heat insulation effects, and have been widely used as materials for blocking infrared rays. [0003] For example, US Patent No. 5,385,751 discloses a fluorine-doped tungsten oxide infrared-blocking material, but the manufacturing method uses chemical vapor deposition (Chemical Vapor Deposition), which has the disadvantages of expensive manufacturing equipment and high ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D5/32C09D133/12C01B13/14
CPCC01G41/006Y02A30/00Y02B30/90Y02P20/10
Inventor 冯殿润徐森煌郑维升
Owner NANYA PLASTICS CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap