Highly bright ceramic glaze

A technology of ceramic glaze and highlighting, which is applied in the field of ceramic glaze to achieve the effect of good smoothness, high aesthetics and low preparation cost

Inactive Publication Date: 2012-10-17
CARLOBBIA GLAZE KUNSHAN
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The surface of the ceramic product is smooth and wear-resistant, but the brightness of the ceramics of the prior art is general. With the improvement of people's living standards, people no longer satisfy the brightness of the existing ceramics. On the basis of this, research and design a high-gloss ceramic glaze with smooth glaze surface and good enamel quality, especially high brightness and good aesthetics, which can meet high requirements and standards.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A bright ceramic glaze made from the following raw materials in parts by weight:

[0018] NaSiO 3 40 parts, NaAl 2 o 3 20 parts, CaCO 3 15 parts, PbO20 parts, BaS 15 parts, LiO 2 6 servings.

Embodiment 2

[0020] A bright ceramic glaze made from the following raw materials in parts by weight:

[0021] NaSiO 3 20 parts, NaAl 2 o 3 10 parts, CaCO 3 5 parts, PbO 10 parts, BaS 10 parts, LiO 2 3 copies.

Embodiment 3

[0023] A bright ceramic glaze made from the following raw materials in parts by weight:

[0024] NaSiO 3 30 parts, NaAl 2 o 3 15 parts, CaCO 3 10 parts, PbO 15 parts, BaS 15 parts, LiO 2 4 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a highly bright ceramic glaze used for preparation of ceramics. The ceramic glaze is prepared from the following raw materials by weight: 20-40 parts of NaSiO3, 10-20 parts of NaAl2O3, 5-15 parts of CaCO3, 10-20 parts of PbO, 10-15 parts of BaS, and 3-6 parts of an alkali metal. By means of a lot of experiments to select and determine the optimal composition and ratio, the highly bright ceramic glaze provided in the invention for preparation of ceramics can be used to prepare ceramics with highly bright glazes and aesthetic appearances, as well as ability to meet the demanding standards of people.

Description

[0001] technical field [0002] The invention relates to a ceramic glaze for preparing ceramics, in particular to a high-brightness ceramic glaze for ceramics. Background technique [0003] The surface of the ceramic product is smooth and has good wear resistance, but the brightness of the ceramics of the prior art is general. With the improvement of people's living standards, people no longer satisfy the existing brightness of the ceramics. Based on this, research and design a high-gloss ceramic glaze with smooth glaze surface and good enamel quality, especially high brightness and good aesthetics, which can meet high requirements and standards. Contents of the invention [0004] Purpose of the invention: The technical problem to be solved by the present invention is to overcome the deficiencies of the prior art and provide a high-brightness glazed glass with good smoothness and good enamel, especially high brightness and good aesthetics, which can meet people's high stan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86
Inventor 赵白弟
Owner CARLOBBIA GLAZE KUNSHAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap