Olefin deoxygenation agent, its preparation method, and olefin deoxygenation method using the same

An olefin deoxidizer and olefin technology, applied in the direction of chemical change purification/separation, organic chemistry, etc., can solve the problems of low deoxidation capacity and short service life, achieve high deoxidation capacity, avoid Ag sintering, and reduce the effect of low temperature

Active Publication Date: 2014-08-27
CHINA PETROLEUM & CHEM CORP +1
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] The purpose of the present invention is to provide a new olefin deoxidizer, its preparation method and application, and an olefin deoxygenation method in order to overcome the defects of low deoxidation capacity and short service life of the existing olefin deoxidizer at room temperature (25° C.)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] On the one hand, the invention provides a kind of preparation method of olefin deoxidizer, described method comprises the following steps:

[0025] (1) Nanoscale TiO modified by manganese source and alkali metal oxide and / or alkali metal hydroxide 2 Mix with the binder to obtain a mixture, respectively, Mn 3 o 4 , Modified nano TiO 2 and binder, based on 100 parts by weight of the manganese source, the modified nano-TiO 2 The dosage is 58-100 parts by weight, the binder is 1.5-25 parts by weight, and the manganese source is Mn 3 o 4 And / or can get Mn after roasting 3 o 4 manganese compounds;

[0026] (2) the mixture obtained in step (1) is first roasted;

[0027] (3) The product after step (2) roasting is impregnated with the aqueous solution of the compound of silver equal volume, then kneading, molding, respectively with Mn 3 o 4 and Ag 2 In terms of O, based on 100 parts by weight of the manganese source, the aqueous solution of the compound of silver is 8...

Embodiment 1

[0063] This example is used to illustrate the preparation method of the olefin deoxidizer provided by the present invention.

[0064] At 650g, the average particle size is 9.8nm and the specific surface area is 160m 2 / g anatase TiO 2 Add sodium hydroxide aqueous solution to carry out equal volume impregnation, with Na 2 In terms of O, the sodium hydroxide aqueous solution was 13 g, and then dried at 100 °C for 10 h to obtain the sodium hydroxide modified TiO 2 , NaOH-modified TiO 2 and MnCO with an average particle size of 35 μm 3 , and the cement with an average particle size of 35 μm is mixed evenly, MnCO 3 , Sodium hydroxide modified TiO 2 and the amount of cement so that the Mn 3 o 4 , Sodium hydroxide modified TiO 2 and cement meter, based on 1000g of MnCO 3 , NaOH-modified TiO 2 650g of cement, 200g of cement, and then carry out the first calcination of the mixture obtained by mixing uniformly at 430°C for 8h, and the modified nano-sized TiO after calcination ...

Embodiment 2

[0067] This example is used to illustrate the preparation method of the olefin deoxidizer provided by the present invention.

[0068] In 580g, the average particle size is 5nm and the specific surface area is 200m 2 / g anatase TiO 2 Add sodium hydroxide aqueous solution to carry out equal volume impregnation, with Na 2 In terms of O, the sodium hydroxide aqueous solution was 18 g, and then dried at 120 °C for 8 h to obtain the sodium hydroxide modified TiO 2 , NaOH-modified TiO 2 MnCO with an average particle size of 20 μm 3 , and the cement with an average particle size of 20 μm is mixed evenly, MnCO 3 , Sodium hydroxide modified TiO 2 and the amount of cement so that the Mn 3 o 4 , Sodium hydroxide modified TiO 2 and cement meter, based on 1000g of MnCO 3 , NaOH-modified TiO 2 is 580g, cement is 150g, and then the mixture obtained by mixing uniformly is subjected to the first roasting at 450°C for 2h, and the modified nano-sized TiO after roasting 2 In, Na 2 The ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an olefin deoxygenation agent, its preparation method, and olefin deoxygenation method using the same. The preparation method includes (by weight parts) (1) mixing manganese source (as Mn3O4) 100, modified titania nanoparticle 58-100 and binder 1.5-25 to obtain a mixture; (2) calcining; (3) kneading the calcined mixture and a silver compound (as Ag2O) aqueous solution 8-35, and forming; (4) aging and drying; and (5) calcining. The inventive olefin deoxygenation agent has high room-temperature deoxygenation capacity, high mechanical crushing strength, low deoxygenation depth, low reduction temperature, and wide applicability in industrial production.

Description

technical field [0001] The invention relates to a preparation method of an olefin deoxidizer, an olefin deoxidizer prepared by the preparation method, an application of the olefin deoxidizer and an olefin deoxygenation method. Background technique [0002] Olefins are important basic organic chemical raw materials. Among them, ethylene and propylene are the main raw materials for the production of polymer materials. With the rapid development of polyethylene and polypropylene technology, various new high-efficiency polyethylene, polypropylene catalysts and metallocene catalysts have been applied to industrial production. In order to avoid poisoning and deactivation of such high-efficiency polyolefin catalysts and improve product quality, there are strict restrictions on the impurity content of ethylene and propylene raw materials used for polymerization. According to the national standard for ethylene and propylene raw materials, the oxygen content in qualified polymer gra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07C7/148C07C11/04C07C11/06
Inventor 吕顺丰刘博黄凤兴秦燕璜李彤王世亮
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com