A kind of mirror ink for automobile glass and preparation method thereof

A technology of mirror ink and automotive glass, which is applied in ink, applications, household appliances, etc. It can solve the problems of rare reports of mirror ink on automotive glass, low gloss of ink, and low gloss, so as to be beneficial to environmental protection and combine Good strength, high gloss effect

Inactive Publication Date: 2014-10-08
IRICO
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most of the products used in the market contain lead, cadmium and other ingredients. Under the current environmental protection situation, the pollution caused by the use of lead and cadmium makes the environment take many years to recover.
On the other hand, the glossiness of common automotive glass inks is not high, and mirror inks suitable for automotive glass are rarely reported.
[0003] In view of the above existing deficiencies in the ink for automotive glass, it is imperative to develop a mirror ink for automotive glass that can replace the existing mirror ink for automotive glass that contains lead and has low gloss.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of mirror ink for automobile glass, its specific preparation is to complete according to the following process steps:

[0022] First prepare the following raw materials according to mass percentage:

[0023] 60% lead-free glass powder, 30% organic vehicle, 2% solvent, 8% pigment.

[0024] Each component of above-mentioned lead-free glass powder is by mass percent:

[0025] SiO 2 6%; B 2 o 3 20%;Al 2 o 3 8%;Na 2 CO 3 3%;K 2 CO 3 20%; CaCO 3 10%; BaCO 3 10%; CuO 10%; ZnO 8%; TiO 2 5%;

[0026] The organic carrier is a mixture formed by dissolving 10% ethyl cellulose in 90% turpentine by mass percentage, the solvent is terpineol, and the pigment is copper chrome black.

[0027] The preparation method of this kind of automotive glass mirror ink is as follows:

[0028] 1) Preparation of lead-free glass powder: first weigh the glass powder raw material according to the above mass percentage, melt and clarify it in a high-temperature melting furnac...

Embodiment 2

[0032] A kind of mirror ink for automobile glass, its specific preparation is to complete according to the following process steps:

[0033] First prepare the following raw materials according to mass percentage:

[0034] 65% lead-free glass powder, 22% organic vehicle, 6% solvent, 7% pigment;

[0035] Each component of above-mentioned lead-free glass powder is by mass percent:

[0036] SiO 2 10%; B 2 o 3 31%;Al 2 O 34%; Na 2 CO 3 20%;K 2 CO 3 5%; CaCO 3 5%; BaCO 37%; CuO 8%; ZnO 6%; TiO 2 4%;

[0037] The above-mentioned organic carrier is a mixture formed by dissolving 20% ​​methyl cellulose in 80% turpentine by mass percentage, the solvent is castor oil, and the pigment is ferrochrome black.

[0038] The preparation method of this kind of automotive glass mirror ink is as follows:

[0039] 1) Preparation of lead-free glass powder: first weigh the glass powder raw material according to the above mass percentage, melt and clarify it in a high-temperature m...

Embodiment 3

[0043] A kind of mirror ink for automobile glass, its specific preparation is to complete according to the following process steps:

[0044] First prepare the following raw materials according to mass percentage:

[0045] 70% lead-free glass powder, 17% organic vehicle, 7% solvent, 6% pigment;

[0046] Each component of above-mentioned lead-free glass powder is by mass percent:

[0047] SiO 2 14%; B 2 o 3 60%;Al 2 o 3 2%;Na 2 CO 3 3%;K 2 CO 3 3; CaCO 3 1%; BaCO 3 3%; CuO 10%; ZnO 2%; TiO 2 2%;

[0048] The above-mentioned organic carrier is a mixture formed by dissolving 20% ​​ethyl cellulose in 80% butyl carbitol acetate by mass percentage, the solvent is castor oil, and the pigment is copper chrome black.

[0049] The preparation method of this kind of automotive glass mirror ink is as follows:

[0050] 1) Preparation of lead-free glass powder: first weigh the glass powder raw material according to the above mass percentage, melt and clarify it in a hig...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to mirror ink for automotive glass and a preparation method of the mirror ink. The mirror ink is characterized by comprising, by mass, 10-30% of organic carriers, 2-8% of solvent, 2-8% of pigment raw materials and the balance unleaded glass powder. The ink for the automotive side windshield glass contains no harmful substances such as lead, cadmium, mercury, hexavalent chromium, PBB (polybrominated biphenyl) and PBDE (polybrominated diphenyl ethers) so as to meet the requirements of social devolvement on environmental protection. The mirror ink has the advantages that the mirror ink gives priority to the unleaded glass powder which contains no elements such as lead, cadmium, mercury and hexavalent chromium harmful to the environment, so that environmental protection is benefited; and the mirror ink is good in wettability, surface smoothness and bonding strength with the glass after sintering and high in shading rate and acid-resistant, has gloss exceeding requirements of general manufacturers and can completely substitute for exiting ink to be used for the field of automotive glass manufacturing.

Description

technical field [0001] The invention relates to a mirror ink for automobile glass and a preparation method thereof. Background technique [0002] There are many types of inks that are seen in daily life, and there are mainly three kinds of inks that are suitable for automobile glass: ink for automobile front windshield, ink for automobile side windshield and ink for automobile rear windshield tempered glass, that is, ink used around the window glass The black part mainly plays the role of decoration and UV protection. At present, most of the products used in the market contain lead, cadmium and other ingredients. Under the current environmental protection situation, the pollution caused by the use of lead and cadmium will take many years to restore the environment. On the other hand, the glossiness of common automotive glass inks is not high, and mirror inks suitable for automotive glass are rarely reported. [0003] In view of the above existing deficiencies in the ink fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/00C09D11/03
Inventor 张宇阳
Owner IRICO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com