Polypropylene composition and preparation method thereof

A technology of polypropylene composition and polypropylene resin, which is applied in the field of polypropylene modification, can solve the problem of high cost and achieve the effect of low cost

Active Publication Date: 2013-03-06
CHINA PETROLEUM & CHEM CORP
View PDF2 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] In the prior art, the rigidity and heat resistance of polypropylene resin are improved by adding a large amount of nucleating agent, and the cost is relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polypropylene composition and preparation method thereof
  • Polypropylene composition and preparation method thereof
  • Polypropylene composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035]

Embodiment 2

[0037]

[0038]

Embodiment 3

[0040]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of polypropylene modification, and particularly relates to a polypropylene composition and a preparation method thereof. The polypropylene composition provided by the invention is prepared from the following raw materials in parts by weight: 100 parts of polypropylene resin, 0.05-2% of heat stabilizer, 0.02-0.5 part of stearic acid metal salt, 0.05-3 parts of inorganic filler and 0.01-0.2 part of organic nucleating agent. The polypropylene resin composition, which is prepared by blending and granulating the polypropylene resin, heat stabilizer, stearic acid metal salt, inorganic filler and slight nucleating agent, has the advantages of high rigidity, high heat resistance and low cost; the preparation technique is simple and easy to implement; and the polypropylene resin composition can be used in the fields of automobiles, home appliances, home furnishing and the like.

Description

technical field [0001] The invention belongs to the field of polypropylene modification, and in particular relates to a polypropylene composition and a preparation method thereof. Background technique [0002] Polypropylene resin is gradually replacing some engineering plastics due to its excellent rigidity and heat resistance, and rich post-modification methods, and is widely used in automobiles, home appliances and households. Especially the impact copolymer polypropylene resin, due to the progress of production technology and catalyst technology, has endowed the product with more excellent comprehensive performance. However, due to the high technical difficulty in the production of impact copolymer polypropylene, especially in terms of product rigidity, toughness and fluidity, it cannot fully meet the needs in some fields, so it is still necessary to develop impact copolymer polypropylene. Post-modification is carried out on the basis of grades, that is, high rigidity, h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/14C08K13/02C08K5/098C08K5/521C08K3/34C08K3/26B29B9/06
Inventor 唐岩李丽李延亮王秀丽
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap