Nano carbon black and nano rare earth synergistic-enhanced metal matrix micro-nano powder and preparation method thereof

A technology of nano-rare earth and nano-carbon black, applied in the field of metal-based micro-nano powder for laser remanufacturing and its preparation, nano-carbon black and nano-rare earth synergistically enhanced metal-based micro-nano powder and its preparation, which can solve the problem of laser absorption rate Low heat input, high heat input, etc., to achieve good application prospects, narrow heat-affected zone, and improved wettability

Inactive Publication Date: 2014-09-17
JIANGSU UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the problem that the existing laser remanufacturing powder has a low absorption rate of laser light, which leads to many limitations of laser remanufacturing technology in the process of remanufacturing thin-walled parts, such as large heat input, and to invent a Nano-carbon black and nano-rare earth synergistically reinforced metal-based micro-nano powder and its preparation method provide a material basis for the wide application of laser remanufacturing technology in the remanufacturing of thin-walled parts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano carbon black and nano rare earth synergistic-enhanced metal matrix micro-nano powder and preparation method thereof
  • Nano carbon black and nano rare earth synergistic-enhanced metal matrix micro-nano powder and preparation method thereof
  • Nano carbon black and nano rare earth synergistic-enhanced metal matrix micro-nano powder and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0040] Materials used in this embodiment: the average particle diameter of nano-carbon black powder is 18nm, the tinting strength is 135%, and the mass fraction is 2%; the nano-rare earth powder is cerium oxide, and its average particle diameter is 20nm, and the mass fraction is 3%; The powder is Al-Si alloy powder, the average particle size is 50 μm, and the mass fraction is 95%; adopt the above-mentioned steps to prepare the metal-based micro-nano powder synergistically reinforced by nano-carbon black and nano-rare earth, and its ball milling composite parameter is that the ball milling speed is 200 rpm / Minutes, the ratio of ball to material is 8:1, and the ball milling time is 1 hour. Observed by scanning electron microscope, the prepared micro-nano powder maintains the spherical characteristics of micro-powder ( figure 1 ), its surface is coated with a large number of nano-carbon black powder and nano-rare earth powder with high dispersion characteristics ( figure 2 ), ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses nano carbon black and nano rare earth synergistic-enhanced metal matrix micro-nano powder and a preparation method thereof. The powder is characterized by comprising the following components in percentage by mass: 0.5-3% of nano carbon black powder, 2-4% of nano rare earth powder and 93-97.5% micron metal powder, wherein the percentage sum of the components is 100%; and core-shell structure micro-nano powder with the micron metal powder as core and with the nano carbon black powder and the nano rare earth powder as shell is formed. The preparation method comprises the following steps: single-phase nano carbon black suspension and single-phase nano rare earth suspension are prepared firstly, and are mixed to form double-phase nano suspension; then the double-phase nano suspension and spherically preprocessed micron metal powder are mixed, milled with balls, and are dried to prepare the metal matrix micro-nano powder. As the nano carbon black and the nano rare earth are synchronously guided in, the adding quantity of the nano carbon black can be further increased, so that better absorptivity for laser is achieved; produced thin-walled pieces have less deformation, narrow heat influence areas and good wear resistance, and can satisfy the requirements of powder conveying through the present laser forming mainstream technology, that is direct powder conveying type laser forming technology; and the powder has stronger engineering practicability and excellent application prospect.

Description

technical field [0001] The invention relates to a metal-based micro-nano powder and a preparation method thereof, in particular to a metal-based micro-nano powder for laser remanufacturing and a preparation method thereof, in particular to a metal-based nano-carbon black and nano-rare earth synergistically reinforced Micro-nano powder and its preparation method. Background technique [0002] On May 13, 2010, 11 ministries and commissions including the National Development and Reform Commission, the Ministry of Science and Technology, and the Ministry of Industry and Information Technology jointly issued a document to promote the development of the remanufacturing industry, raising the development of remanufacturing projects to a basic national policy for realizing my country's sustainable development strategy. As the first to advocate and actively promote remanufacturing engineering in China, Professor Xu Binshi, an academician of the Chinese Academy of Engineering, clearly ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F1/00
Inventor 王宏宇沈清袁晓明黎向锋吴志奎许瑞华程满金镜张凯
Owner JIANGSU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products