Banana peel extract carbon steel acid pickling inhibitor and application thereof

A technology of pickling corrosion inhibitor and banana peel, which is applied in the field of corrosion inhibitor production, can solve the problems of not having market competitiveness, not adapting to global environmental protection requirements, toxic and side effects of cleaning agents, etc., to prevent excessive corrosion, Long-lasting effect with low dosage

Inactive Publication Date: 2013-04-24
INST OF OCEANOLOGY - CHINESE ACAD OF SCI
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Currently commonly used cleaning agents mainly include toxic inorganic corrosion inhibitors such as chromate, nitrate, and nitrite, as well as some organic phosphorus corrosion inhibitors, whose discharge may cause eutrophication of water bodies. Most cleaning agents have toxic and side effects, do not have market competitiveness, and do not meet the worldwide environmental protection requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The pickling solution is dilute hydrochloric acid, the concentration is 0.1M, the amount of pickling solution is 100L, add 30g of banana peel extract, and immerse the steel to be cleaned in the pickling solution for 4 hours at room temperature.

[0022] The highest corrosion inhibition efficiency obtained through experimental testing is 97%, which shows that it is an efficient cleaning agent.

Embodiment 2

[0024] The pickling solution is dilute hydrochloric acid, the concentration is 0.1M, the amount of pickling solution is 100L, add 15g of banana peel extract, and immerse the steel to be cleaned in the pickling solution for 4 hours at room temperature.

[0025] The highest corrosion inhibition efficiency obtained through experimental testing is 96%, which shows that it is an efficient cleaning agent.

Embodiment 3

[0027] The pickling solution is dilute hydrochloric acid, the concentration is 0.5M, the amount of pickling solution is 100L, add 30g of banana peel extract, and immerse the steel to be cleaned in the pickling solution for 4 hours at room temperature.

[0028] The highest corrosion inhibition efficiency obtained through experimental testing is 95%, which shows that it is an efficient cleaning agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a carbon steel acid pickling inhibitor and application thereof. The carbon steel acid pickling inhibitor is used for preventing carbon steel and products thereof from unnecessary corrosion and acid liquor consumption in an acid pickling process. The inhibitor is an organic mixture in a banana peel extract. The application method of the inhibitor is characterized in that the cleaning liquor is diluted hydrochloric acid with concentration of 0.10-1.0kmol / m<3>, 0.010-2.0kg / m<3> of cleaning agent is added, the temperature is controlled between 25 DEG C and 30 DEG C, and carbon steel and products thereof to be cleaned are added and are immersed for 1-4 hours. The product is used for cleaning surfaces of carbon steel and products thereof, can prevent excessive erosion of metals and excessive consumption of acid liquor in a cleaning process, and has the prominent advantages of low dosage, high efficiency and strong sustained action capacity.

Description

technical field [0001] The invention relates to the technical field of corrosion inhibitor production, in particular to a kind of green banana peel extract that is used to prevent carbon steel and its products from unnecessary corrosion and acid consumption in the pickling process agents and their applications. Background technique [0002] Steel is used more and more widely. In the process of product processing and application, dilute sulfuric acid or dilute hydrochloric acid is often used to clean the surface to remove the oxide film or corrosion products on the surface. Since strong acid has a corrosive effect on metal equipment, it is often used in the pickling process. The phenomenon of "over-corrosion" occurs. This process will not only cause corrosion of metal materials, but also produce a large amount of acid, which will cause serious damage to the environment. In order to avoid excessive consumption of metal or acid during pickling and prevent harmful corrosion, it...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23G1/06C23G1/08
Inventor 庞雪辉魏琴井改革隋卫平解建东侯保荣
Owner INST OF OCEANOLOGY - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More