Manufacturing method for large azure stone wall

A manufacturing method and technology for glazed walls, applied in glass manufacturing equipment, glass production, manufacturing tools and other directions, can solve the problems of color difference bubbles in large glazed handicrafts, save the steps of preparing wax film, simple and convenient operation, and reduce production costs Effect

Active Publication Date: 2015-05-13
湖州艾迪特琉璃工艺品有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a method for making a large-scale glazed wall to solve the technical problem that defects such as color difference bubbles are likely to occur when using the prior art to make large-scale glazed handicrafts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A method for making a large glazed wall, comprising the following steps:

[0032] Design the effect drawing according to the requirements, make the steel structure base plate according to the size of the effect drawing, and lay the flat plate;

[0033] The size of the effect drawing is 4.5m×1.5m, and the size of the steel structure bottom plate is also 4.5m×1.5m;

[0034] Use clay to carve reliefs on the flat plate according to the renderings;

[0035] Spread the oil mud on the flat plate, and then finely carve the relief according to the rendering;

[0036] Turn the completed mud sample into a high-temperature plaster mold, and add reinforced steel structure and high-temperature-resistant structural materials into the high-temperature plaster mold to ensure the thermal stability of the high-temperature plaster mold;

[0037] The mud sample refers to the mud sample carved out of oil mud, and turning over the mold belongs to the conventional technical means of th...

Embodiment 2

[0046] A method for making a large glazed wall, comprising the following steps:

[0047] Design the effect drawing according to the requirements, make the steel structure base plate according to the size of the effect drawing, and lay the flat plate;

[0048] The size of the effect drawing is 4.5m×1.5m, and the size of the steel structure bottom plate is also 4.5m×1.5m;

[0049] Use clay to carve reliefs on the flat plate according to the renderings;

[0050] Spread the oil mud on the flat plate, and then finely carve the relief according to the rendering;

[0051] Turn the completed mud sample into a high-temperature plaster mold, and add reinforced steel structure and high-temperature-resistant structural materials into the high-temperature plaster mold to ensure the thermal stability of the high-temperature plaster mold;

[0052] The mud sample refers to the mud sample carved out of oil mud, and turning over the mold belongs to the conventional technical means of th...

Embodiment 3

[0061] A method for making a large glazed wall, comprising the following steps:

[0062] Design the effect drawing according to the requirements, make the steel structure base plate according to the size of the effect drawing, and lay the flat plate;

[0063] The size of the effect drawing is 4.5m×1.5m, and the size of the steel structure bottom plate is also 4.5m×1.5m;

[0064] Use clay to carve reliefs on the flat plate according to the renderings;

[0065] Spread the oil mud on the flat plate, and then finely carve the relief according to the rendering;

[0066] Turn the completed mud sample into a high-temperature plaster mold, and add reinforced steel structure and high-temperature-resistant structural materials into the high-temperature plaster mold to ensure the thermal stability of the high-temperature plaster mold;

[0067] The mud sample refers to the mud sample carved out of oil mud, and turning over the mold belongs to the conventional technical means of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a manufacturing method for azure stone handicrafts, and particularly relates to a manufacturing method for a large azure stone wall. The manufacturing method for the large azure stone wall includes the following steps: 1), paving a flat plate on a flat base plate of a steel structure; 2), carving embossments on the flat plate with greasy filth; 3), making a high-temperature plaster mould from an accomplished greasy filth sample; 4), placing the mould horizontally into a calcinator; 5), placing azure stone materials in various colors into corresponding parts of the high-temperature plaster mould in proportion sequentially; 6), performing calcination; 7), grinding azure stone surfaces manually after azure stones are discharged from the calcinator, performing flat surface grinding with a flat-grinding machine and edging with an edge grinding machine, and cutting the azure stones to be of required sizes with a cutting machine; and 8), processing the whole wall through two abrasive blasting processes including coarse sanding and fine sanding, and accomplishing post stage processing through chemical surface treatment. The azure stone handicrafts manufactured with the manufacturing method have the advantage of being large-sized, attractive, flawless, and the like. The manufacturing method for the large azure stone wall is suitable for manufacturing of decorative walls.

Description

technical field [0001] The invention relates to a manufacturing method of glazed handicrafts, in particular to a manufacturing method of a large glazed wall. Background technique [0002] In the prior art, when producing glazed handicrafts, it is necessary to use resin and wax as a medium to turn over the samples, turn them into plaster molds, and then use the plaster molds for production. The prior art has no experience in producing large-scale glazed handicrafts. The larger the glazed product, the more prone to flaws, such as color difference and air bubbles. Adopt prior art to produce large-scale colored glaze handicraft and can't avoid producing above-mentioned defect. For example, the Chinese invention patent whose application number is 201110137296.8 discloses a manufacturing process of glazed handicrafts, comprising the following steps: According to the shape of the colored glaze, design the design drawing of the metal parts suitable for the colored glaze used to i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03B19/00B44C5/00
CPCY02P40/57
Inventor 李锋
Owner 湖州艾迪特琉璃工艺品有限公司