High-stability hollow fibrous membrane and preparation method thereof

A high stability, fiber membrane technology, applied in the field of composite materials, can solve the problems of poor stability, low retention rate, poor tensile strength, etc., and achieve the effects of improved stability, simple process and easy control.

Active Publication Date: 2015-05-20
ZHEJIANG CHANGXING CREFLUX MEMBRANE TECH CO LTD
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the defects of poor tensile strength, low rejection rate and poor stability in the prior art hollow fiber membrane, the present invention provides a hollow fiber membrane with high tensile strength, high rejection rate and high stability and a preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-stability hollow fibrous membrane and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A high-stability hollow fiber membrane includes polyvinylidene fluoride membrane filaments, and cross-linked products are evenly embedded in the interior of the polyvinylidene fluoride membrane filaments and the apertures. The cross-linked product is formed by cross-linking polyvinyl alcohol and glutaraldehyde.

[0023] A kind of preparation method of hollow fiber membrane of high stability, such as figure 1 The shown technological process comprises the following steps:

[0024] 1) Polyvinyl alcohol and water are configured into a polyvinyl alcohol aqueous solution with a concentration of 15% by mass;

[0025] 2) Take 30g of polyvinyl alcohol aqueous solution and add it to 500ml of dimethylacetamide, keep the temperature at 65°C, stir evenly, then add 150g of polyvinylidene fluoride powder, continue to keep the temperature at 65°C and stir evenly;

[0026] 3) Add 20g of pore forming agent PVP and 10g of surfactant Tween 80 to the mixed solution obtained in step 2), st...

Embodiment 2

[0035] A high-stability hollow fiber membrane includes polyvinylidene fluoride membrane filaments, and cross-linked products are evenly embedded in the interior of the polyvinylidene fluoride membrane filaments and the apertures. The cross-linked product is formed by cross-linking polyvinyl alcohol and glutaraldehyde.

[0036] A kind of preparation method of hollow fiber membrane of high stability, such as figure 1 The shown technological process comprises the following steps:

[0037] 1) Polyvinyl alcohol and water are configured into an aqueous solution of polyvinyl alcohol with a concentration of 18% by mass;

[0038] 2) Take 40g of polyvinyl alcohol aqueous solution and add it to 500ml of dimethylacetamide, keep the temperature at 75°C, stir evenly, then add 160g of polyvinylidene fluoride powder, continue to keep the temperature at 75°C and stir evenly;

[0039] 3) Add 40g of pore-forming agent PVP and 20g of surfactant Tween 80 to the mixed solution obtained in step 2)...

Embodiment 3

[0047] A high-stability hollow fiber membrane includes polyvinylidene fluoride membrane filaments, and cross-linked products are evenly embedded in the interior of the polyvinylidene fluoride membrane filaments and the apertures. The cross-linked product is formed by cross-linking polyvinyl alcohol and glutaraldehyde.

[0048] A kind of preparation method of hollow fiber membrane of high stability, such as figure 1 The shown technological process comprises the following steps:

[0049] 1) Polyvinyl alcohol and water are configured into a polyvinyl alcohol aqueous solution with a concentration of 14% by mass;

[0050] 2) Take 35g of polyvinyl alcohol aqueous solution and add it to 500ml of dimethylacetamide, keep the temperature at 85°C, stir evenly, then add 170g of polyvinylidene fluoride powder, continue to keep the temperature at 85°C and stir evenly;

[0051] 3) Add 30g of pore-forming agent PVP and 15g of surfactant Tween 80 to the mixed solution obtained in step 2), st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of composite materials, in particular to a high-stability hollow fibrous membrane which comprises polyvinylidene fluoride membrane yarns; and crosslinked products are uniformly embedded inside the polyvinylidene fluoride membrane yarns and in the apertures. The invention further discloses a preparation method of the high-stability hollow fibrous membrane. The preparation method comprises the following steps: allocating PVA water solution; allocating membrane casting liquid and defoaming; allocating core liquid; and spinning to prepare the membrane, wherein during the spinning process, PVA in the membrane casting liquid is crosslinked with glutaraldehyde in the core liquid to cause the crosslinked products to exist in the hollow fibrous membrane stably. The crosslinked products uniformly embedded inside the polyvinylidene fluoride membrane yarns and in the apertures adopt uniform and compact structures, and exist in the hollow fibrous membrane stably, so that the tensile strength, the reject rate and the stability of the membrane yarns are improved. The preparation method has the advantages of simple, safe, efficient and easily-controlled process.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to a highly stable hollow fiber membrane and a preparation method thereof. Background technique [0002] Traditional sewage regeneration treatment technology has disadvantages such as low water quality, large land occupation, and poor stability. Membrane separation technology has the advantages of low energy consumption, simple process, high separation efficiency, and no environmental pollution. It is an important high-tech solution to contemporary energy, resource and environmental problems. It cannot be replaced by any other chemical separation technology. Its application has been It has been involved in chemical, food, pharmaceutical, biochemical, environmental protection and other fields, and has made important contributions to energy conservation, efficiency improvement, and environmental purification. [0003] However, the existing hollow fiber membranes general...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D71/34B01D67/00B01D69/08
Inventor 郑子龙包进锋张星星
Owner ZHEJIANG CHANGXING CREFLUX MEMBRANE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com